Transverse Direction Loading Effect on the Elasticity and Strength of Micro and Nano Silica Oxide Composites

Abstract

Using three-point bending experiments, the effect of the particle size of SiO2 on the flexural properties of epoxy composites was investigated. Young modulus and flexural strength were studied for different weight percentage of filler (2,4,6,8 and 10) wt%.The size of SiO2 particles varied from micro (100um) to nano (12nm) . Flexural strength and Young modul were found to increase with the filler content, but when the particle size decreased to the nanoscale, the Young module increased. Flexural strength was higher for microcomposites than nanocomposites.