TY - JOUR ID - TI - Effect of immersion in chemical solution on the mechanical & physical properties for composite material reinforced by Nano alumina Particles تأثير الغمر في المحاليل الكيميائية على الخواص الميكانيكية والفيزيائية لمتراكبات بوليمرية مدعمة بدقائق نانو الومينا AU - Huda .J.Abd AL-Hussien هدى جبار عبد الحسين PY - 2015 VL - 56 IS - 3A SP - 1952 EP - 1963 JO - Iraqi Journal of Science المجلة العراقية للعلوم SN - 00672904 23121637 AB - In this research Epoxy resin was reinforced by nano alumina (AL2O3) particles in grain size(25-30 nm) with two weight ratios (2,4)% then compared with pure Epoxy. Four mechanical tests were performed on these materials include Hardness, flexural, impact & compression strengths before and after immersion in tap water and chemical solutions (CH3COOH) acid, (KOH) base at (0.5N) ,The diffusivity coefficients of all prepared samples were calculate after immersion in water and chemical solutions mentioned above , the results were showed that the Flexural, Impact & Hardness increase after addition the ceramic particles (AL2O3) while the immersion process results showed illustrated different values from sample to other.

في هذا البحث تم تدعيم راتنج الايبوكسي بدقائق نانو الومينا (AL2O3) وبحجم حبيبي (25-30 nm) وبنسبتين وزنيتين (%2,%4) وتم مقارنتها بالايبوكسي النقي. اجريت اربعة اختبارات ميكانيكية على تلك المواد تشمل متانة الانحناء و الصدمة و الصلادة والانضغاطية قبل وبعد غمرها في الماء العادي و المحاليل كيميائية والمتمثلة )بحامض الخليك (CH3COOH والمحلول القاعدي KOH ) ) وبمعيارية (N0.5) وقد تم حساب معاملات الانتشار للنماذج المحضرة بعد غمرها في الماء و المحاليل المذكورة اعلاه. وقد بينت النتائج بان متانة الانحناء و الصدمة والصلادة تزداد بعد اضافة الدقائق السيراميكية (AL2O3) في حين اظهرت نتائج عملية الغمر قيم مختلفة من نموذج لاخر . ER -