TY - JOUR ID - TI - A Comparative Corrosion Studies of Aluminum Metal Matrix Composites Reinforced with nano (Al2O3 and SiC) Particles In Fao Water دراسة مقارنة معدل التاكل للمواد المعدنية المتراكبة ذات اساس المنيوم المقواة بدقائق نانوية للالومينا وكاربيد السليكون في ماء الفاو AU - Mohammed Saieed Waheed AU - Niveen J. Abdalkadir PY - 2015 VL - 33 IS - 4 Part (B) Scientific SP - 723 EP - 732 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - In the present investigation, the static electrochemical corrosion behavior of nano (Al2O3)P and nano (SiC)P based aluminum in Fao water was compared. The nanocomposites were fabrication using liquid metallurgy technique. The effect of nanoparticulates weight percentage (5%, 15% and 25%) on the corrosion was studied. The results showed that the Al reinforced with nano (Al2O3) composites exhibited lower corrosion rates that the Al reinforced with nano (SiC)Pcomposites.The corrosion rate was found to be increased by increasing of the weight percentage of the nanoparticles more than 5% nano (Al2O3)P composites exhibited the highest corrosion resistance among all the investigated nanocomposites.

تم في هذا البحث تقييم سلوك التاكل الكهروكيمياوي الساكن للالمنيوم النقي (1060) المقوى بدقائق نانوية من الالومينا وكاربيد السليكون في ماء الفاو والمقارنة بينهما. حضرت المواد المتراكبة المدعمة بدقائق نانوية بتقنية ميتالورجيا الحالة السائلة حيث تم دراسة تأثير النسب الوزنية للدقائق النانوية (5% و 15%و 25%) على سلوك التاكل. اظهرت النتائج ان المادة المتراكبة المنيوم- نانو الومينا اقل معدل تاكل من المادة المتراكبة المنيوم- نانو كاربيد السليكون في ماء الفاو. كذلك وجد ان معدل التاكل يزداد مع زيادة النسب الوزنية للدقائق النانوية الاكبر من 5% والمقواة بدقائق الالومينا النانوية والتي ابدت اكثر مقاومة تاكل من بقية المواد المتراكبة النانوية. ER -