TY - JOUR ID - TI - Behavior of A.C conductivity and Complex dielectric constant of ZnS Thin Films سلوك التوصيلية الكهربائية AC وثابت العزل الكهربائي للاغشية لكبريتيد الخارصين الرقيقة ZnS AU - Zainab Taha A AU - Khitam S. Shaker AU - Suaad S. Shaker AU - Raghdaa Hameed Hani PY - 2015 VL - 33 IS - 4 Part (B) Scientific SP - 745 EP - 752 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - The effect of temperature on dielectric properties of the prepared ZnS thin films by chemical bath deposition at film thickness (200) nm deposited at substrate temperature 333 K, was measured at frequency range (0.04-10 MHz) in the temperature range (298- 473) K .The temperature – dependent of electrical conductivity, the real and imaginary parts of the complex dielectric constant are calculated at the selected frequencies. The frequency exponent n, and the activation energy, Ea, are determined. The a.c. conduction mechanism of ZnS films has been explained on the basis of hopping of charge carriers.

تأثير درجة الحرارة على خصائص العازلة للكهربائيةللأغشية الرقيقة ZnSالمرسبة بطريقة الترسيب الحمام الكيميائيلغشاء ذات سماكة (200) نانومتر ومرسب على ركيزة في درجة حرارة 333 K، تم القياس في مدى التردد (0،04 حتي 10 ميغاهيرتز) في نطاق درجات الحرارة (298- 473 ) K. تم حساب درجة الحرارة -المعتمدةعلى التوصيلية الكهربائية، والأجزاء حقيقية والخيالية لثابت العزل الكهربائي المعقد في ترددات محددة. كما وتم تحديد مركبة التردد، وطاقة التنشيط،. تم توضيح ميكانكية التوصيل الكهربائي المتناوب للاغشية الرقيقة على أساس التنقل من حاملات الشحنة. ER -