TY - JOUR ID - TI - Effect of Differential Speed Rolling Temperature into Mechanical Properties of AZ31B Magnesium Alloy تأثير درجة حرارة الدرفلةغير المتماثلةعلى الخواص الميكانيكية لسبيك المغنيسيوم AZ31B AU - Emad A. Hussein AU - Azal R. Ismail PY - 2016 VL - 34 IS - 1 Part (A) Engineering SP - 1 EP - 11 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - The received AZ31B magnesium alloy sheets of 2 mm in thickness were subjected to differential speed rolling (DSR) process performed on a mill, of which the rotation speed ratio of the lower roll and upper one is kept at constant 1.15, by using the different upper and lower roller diameters. The influence of the rolled sheet temperature on the microstructure of the specimens was examined by optical microscopy, and elongation-to-failure of tensile test at temperature 623 K and initial strain-rate range between 0.5×10-3 - 1.83×10-3 s-1 was measured. The present process was found to be effective to refine the grain size. Grain refinement became more marked and uniform. The sheet DSRed at 473K exhibited the highest values of 340% and 0.35 for elongation-to-failure and strain rate sensitivity (m) respectively.

صفيحة مغنيسيوم AZ31B بسمك 2ملم خضعت الى عملية درفلة بسرع متفارقة (سرعة درافيل غير متماثلة), بنسبة سرعة ثابتة مابين الدرفيلين الاسفل الى الاعلى 1.15 عن طريق استخدام اقطار مختلفة للدرفيلين. تأثير درجة حرارة الدرفلة على التركيب المجهري للعينات تم فحصه باستخدام المجهر البصري, وتم قياس الاستطالة حتى الفشل لاختبار الشد عند درجة حرارة 623 كلفن ومعدلات أنفعال أولية مابين 0.5x-310 – 1.83x-310 ثا-1 .أظهرت النتائج أن عملية الدرفلة المتفارقة فعالة في تنعيم الحجم البلوري وأصبحت البلورات أكثر أنتظاماً ووضوحاً. أظهرت الصفيحة المدرفلة بدرجة حرارة 473 كلفن أعلى قيم لكل من الاستطالة حتى الفشل وحساسية معدل أنفعال (m) حيث كانت 340% و 0.35 على التوالي. ER -