TY - JOUR ID - TI - Studying The Optical Properties of CdO and CdO: Bi Thin Films دراسة الخواص البصريه لاغشية أوكسيد الكادميوم ( CdO ) غيرالمشوبة والمشوبة بالبزموث (Bi) AU - Zain A. Muhammad زين العابدين ماجد محمد AU - Ahmed T. Hassan احمد طالب حسن AU - Yasmeen Z. Dawood ياسمين زيدان داود PY - 2016 VL - 13 IS - 3 SP - 593 EP - 598 JO - Baghdad Science Journal مجلة بغداد للعلوم SN - 20788665 24117986 AB - Cadmium Oxide and Bi doped Cadmium Oxide thin films are prepared by using the chemical spray pyrolysis technique a glass substrate at a temperature of (400⁰C) with volumetric concentration (2,4)%. The thickness of all prepared films is about (400±20) nm. Transmittance and Absorbance spectra are recorded in the wave length ranged (400-800) nm. The nature of electronic transitions is determined, it is found out that these films have directly allowed transition with an optical energy gap of (2.37( eV for CdO and ) 2.59, 2.62) eV for (2% ,4%) Bi doped CdO respectively. The optical constants have been evaluated before and after doping.

حضرت أغشية أوكسيد الكادميوم ( CdO ) غيرالمشوبة والمشوبة بالبزموث (Bi) باستخدام طريقة التحلل الكيميائي الحراري على قواعد منْ الزجاج بدرجة حرارة القاعدة (400⁰C) وبنسب حجمية مختلفة %(2,4)، وكان سمك الاغشية المحضرة بحدود nm(400±20 ). تمت دراسة الخصائص البصرية للأغشية من خلال تسجيل طيفي الامتصاصية والنفاذية ولمدى الأطوال الموجية nm(800-400). تم تعيين طبيعة الانتقالات الالكترونية ووجد انها انتقالات مباشرة مسموحة, وكانت قيمة فجوة الطاقة البصريه لاوكسيد الكادميوم الغيرمشوب eV(2.37) والمشوب بالبزموث eV(2.59, 2.62) للنسب الحجمية ( (2% ,( (4% على التوالي. كما تم حساب الثوابت البصرية قبل وبعد التشويب. ER -