TY - JOUR ID - TI - The effect of Cadmium Substitution on the structural and magnetic properties of Nickel Ferrite دراسة تأثير الأيونات الاستبدالية للكادميوم على الخواص التركيبية والمغناطيسية للمركب نيكل- فرايت AU - خلف إبراهيم خليل الجبوري PY - 2016 VL - 21 IS - 2 SP - 155 EP - 161 JO - Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة SN - 18131662 24151726 AB - Nickel – Cadmium ferrites having the chemical formula (Ni1-xCdxFe2O4), (0 ≤ X ≤ 0.5) were prepared by using powders technology method. The particle size of the ferrite samples were estimated from X-ray diffraction studies after the confirmation of the formation of single phase spinel structure of the ferrites. We found that the Lattice constant and density (ρx-ray) increased with Cd content while the porosity was noticed to decrease. Also the magnetic testing showed decreases in values the Coercive Force from (0.408 KA/m) to (0.384 KA/m) and the Remnant Magnetization from (0.056 Tesla) to ( 0.048 Tesla) and the Magnetic Relative permeability is the within range (0.137 ~ 0.125) with increasing of the Cadmium concentration while the Magnetic Susceptibility was noticed to increase from (0.862) to (0.875).

تم تحضير مركبات النيكل – كادميوم ذات الصيغة الكيميائية Ni1-xCdxFe2O4 حيث ان 0 ≤ X ≤ 0.5 وذلك باستخدام طريقة تكنلوجيا المساحيق. تم حساب الحجم الحبيبي لجميع مركبات الفرايت المحضرة من حيود الأشعة السينية بعد التأكد من تشكيل الطور الأحادي ذو التركيب البلوري مغزلي الشكل. كما تم حساب ثابت الشبيكة و الكثافة الظاهرية المحسوبة من حيود الأشعة السينية (ρx-ray),حيث وجد أنها تزداد مع زيادة تركيز نسبة الكادميوم, بينما كانت المسامية تنقص مع زيادة تركيز الكادميوم. أما نتائج الفحوصات المغناطيسية فقد أظهرت نقصان قيم القوة القاهرة (0.408 ~ 0.384 KA/m) و المغناطيسية المتبقية (0.056 ~ 0.048 Tesla)والنفوذية المغناطيسية (0.137 ~ 0.125) مع زيادة تركيز الكادميوم بينما أدى إلى زيادة قيم التأثرية المغناطيسية(0.862 ~ 0.875) . ER -