TY - JOUR ID - TI - Effect of Cobalt content on mechanical properties of Al-Si alloy تأثير محتوى الكوبلت على الخواص الميكانيكية لسبيكة المنيوم-سليكون AU - Maryam A.B مريم عبد العظيم باقر علي PY - 2014 VL - 2 IS - 1 SP - 46 EP - 58 JO - Wasit Journal of Engineering Sciences مجلة واسط للعلوم الهندسية SN - 23056932 AB - This work encompasses studying the effect of different contents of Co on Al-Si alloy with Sb modification prepared by stir casting method. The content of Co is varying from 0 to 1.2wt%, The effect of Cobalt on microstructure, micro hardness, tensile strength and wear rate were studied extensively. The results show that the intermetallic compounds was increased with the increasing of Cobalt content .The Co-bearing compounds presented as small block shape at first and gradually turned into dendrite or fish bone shape. The addition of Co has appositive effect on tensile strength of the Al-Si alloys that used in the current research, the maximum tensile strength was (177MPa) when Co content was 0.9%Co at room temperature as well as wear rate were studied in this paper and noticed that the addition at 0.9%Co had the better effect at low and high load(5N),(10N).

البحث الحالي يركز على دراسة تأثير اختلاف محتوى الكوبلت على سبيكة المنيوم –سليكون المحورة بالانتيمون التي تم تحضيرها بطريقة السباكة بالتحريك محتوى الكوبلت تراوح بين 0 و1.2% , تأثير الكوبلت على التركيب المجهري ، الصلادة،مقاومة الشد ومعدل البلى تم دراسته ، اظهرت النتائج بان المركبات المعدنية الداخلية تزداد بزيادة محتوى الكوبلت . مركبات الكوبلت تمثل كقطع صغيرة الشكل عند البداية وتتحول تدريجيآ الى الشكل الشجيري او بشكل عظم السمك . اضافة الكوبلت له تأثير ايجابي على مقاومة الشد لسبائك المنيوم-سليكون المستخدمة في البحث الحالي،أعلى مقاومة شد كانت 177 ميكاباسكال عند اضافة 0.9% من الكوبلت عند درجة حرارة الغرفة علاوة الى دراسة معدل البلى حيث لوحظ ان اضافة 0.9% كوبلت له افضل تأثير عند الحمل الواطئ والعالي (5نيوتن),(10نيوتن). ER -