TY - JOUR ID - TI - Dielectric and optical behaviors for pure potassium sulfate and doped with copper and iron السلوكيات العزلية والبصرية لكبريتات البوتاسيوم K2SO4)) النقية والمطعمة بالنحاس والحديد AU - Tariq A. Al- Dhahir طارق عبد الرضا الظاهر AU - Maryam E. Al-Mahdawi مريم عيسى المهداوي PY - 2016 VL - 57 IS - 3A SP - 1699 EP - 1706 JO - Iraqi Journal of Science المجلة العراقية للعلوم SN - 00672904 23121637 AB - Dielectric measurements were carried on pure and doping potassium sulfate with copper and iron ions samples at 1wt.% and 3wt.% for both of copper and iron. The dielectric constant (ε') decreases exponentially from 2.8 to 1.5 as frequency increase for both dopant which is attributed to the space charge and structural distortion. The dielectric loss (ε") for Cu dopant decrease gradually with frequency. The same behavior for 1%Fe dopant while its 3%Fe doping started from 0.27 then decrease exponential. Band gaps for all samples almost constant around 6 eV.

تم اجراء القياسات العزلية لكبريتات البوتاسيوم النقية والمطعمة بالنحاس والحديد ب بنسبة 1wt.% و 3wt.% لكلا من النحاس و الحديد. ثابت العزل الكهربائي(ε') يقل اسياً من 2,8 الى 1,5 بزيادة التردد لكلا التشويب والذي يعزى الى شحنه الفراغ والتشويه التركيبي , ان عامل الخسارة (ε ") لحالة التطعيم بالنحاس لكلا النسبتين يقل تدريجيا ً مع التردد ويسلك نفس السلوك في حالة 1wt.% للحديد بينما في حالة 3wt.% تبدا من 0,27 ويقل اسيا ً , اما فجوة الطاقة لكل النماذج تبقى ثابتة تقريبا حوالي 6 الكترون-فولط ER -