TY - JOUR ID - TI - PREPARATION OF COPPER-ALUMINA ELECTRICAL CONTACT MATERIALS تحضير مواد موصلة كهربائيا نحاس-الومينا AU - Osama Abdel Bari Haydar A. H. Al-Ethari Abdul Raheem K. Abd Ali اسامة عبد الباري حيدر عبد الحسن العذاري عبد الرحيم كاظم عبد علي PY - 2016 VL - 16 IS - 4 SP - 394 EP - 403 JO - Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد SN - 20761819 AB - Electrical contact material are used in variety of application such as electrical switches ,contactors, circuit breakers, voltage regulators .In this paper copper with different weight percentage of α-alumina composite are prepared by using powder metallurgy technique. Disk samples of 14mm and 10mm in diameter and 5mm thickness. 5, 10, 15, 20, 30 weight percentage of α-alumina have been prepared. Tests including microstructure analyses by scanning electron microscope and optical microscope, electrical resistance, hardness, and dry sliding wear had been carried out. It’s clear that the hardness and electrical resistance increase with increasing additive percentage while wear rate decrease with increasing additive percentage until 15% α-alumina where the wear rate increases .

مواد التلامس الكهربائي تستخدم في عدة تطبيقات مثل المفاتيح الكهربائيه , القواطع الكهربائيه ومنظمات الفولتيه . في هذا البحث تم تحضير مادة مركبة ذات اساس نحاس مع اضافة نسب مختلفة من الالومينا بأستخدام تكنلوجيا المساحيق. تم تحضير عينات اسطوانية بأقطار 14ملم و 10 ملم وذات سمك 5 ملم وكانت نسبة اضافة الالومينا (5, 10, 15, 20, 30) نسبة وزنية . تضمنت الاختبارات اختبار البنية المجهرية باستخدام مجهر المسح الالكتروني و المجهر الضوئي, المقاومة الكهربائية, الصلادة و البلى الانزلاقي الجاف . اشارت النتائج الى زيادة الصلادة والمقاومة الكهربائية بزيادة نسبة الاضافة من الالومينا بينما معدل البلى قل بزيادة نسبة الاضافة وصولا الى نسبة 15% الومينا بعدها يبدأ معدل البلى بالزيادة ER -