TY - JOUR ID - TI - A Study of compression strength and flexural strength for Polymer Concrete دراسة خاصية الانضغاط وخاصية الانحناء للبوليمر كونكريت AU - Mohamed R .Mohamed محمد راضي محمد AU - Sewench Noor ALdeen سه وينج نور الدين رفيق AU - RawabiI Abdulrazzaq روابي عبد الرزاق خماس PY - 2016 VL - 57 IS - 4B SP - 2677 EP - 2684 JO - Iraqi Journal of Science المجلة العراقية للعلوم SN - 00672904 23121637 AB - Polymer concrete were prepared by mixing epoxy resin with sand particles in three different grain size (150-300) , (300-600 ) and (600- 1200) μm respectively. The percentage of epoxy was 15%, 20 %, 25% and 30% wt of the total weight. Compression strength and flexural strength tests were carried out for the prepared samples. The percentages of epoxy resin at 20% wt and 25% wt showed best mechanical properties for all grain sizes. These percentages were adopted to fill the voids between particles sand have two different size ranges (150-600) μm and {(150-300) & (600-1200)} μm respectively to obtain more dense material. The results showed that the strength of polymer composite at 20% resin is higher than 25% resin.

حضر البوليمر كونكريت بواسطة خلط راتنج الايبوكسي مع الرمل فقط لثلاث احجام حبيبية مختلفة هي (150-300) و(300-600) و (600-1200) مايكرون على التوالي , حيث كانت نسبة الايبوكسي 15% ,20% ,25% ,30%نسبة وزنية من الوزن الكلي , ثم تم اجراء فحوصات مقاومة الانضغاط والانحناء للعينات المحضرة, وقد اظهرت النتائج بأن نسب راتنج الايبوكسي عند20 % و25% تمثل افضل خصائص ميكانيكية لكل الاحجام الحبيبية . تم اختيار هذه النسب لملئ الفراغات بين حبيبات الرمل التي تمتلك حجمين مختلفين(150-600) و}(150-300) &(600-1200 ){ مايكرون على التوالي للحصول على مادة ذات كثافة اكبر. اظهرت النتائج بأن مقاومة الانضغاط والانحناء للعينات عند النسبة 20% كانت اعلى من تلك عند 25% . ER -