TY - JOUR ID - TI - Influence of Heat Treatment on Wear and Hardness Properties of MWCNTs Reinforced Epoxy nanocomposites. تأثير المعاملة الحرارية على خاصية البلى والصلادة لمتراكبات أنابيب الكاربون النانوية المدعمة براتنج الايبوكسي AU - Khalid R. Al-Rawi خالد رشاد الراوي AU - Noor H. Madhi نور هاشم ماضي PY - 2016 VL - 57 IS - 4C SP - 2891 EP - 2897 JO - Iraqi Journal of Science المجلة العراقية للعلوم SN - 00672904 23121637 AB - Nanocomposite of carbon nanotube add to epoxy resin material of weight fraction ( 0.25, 0.5, 0.75 1.0, 1.25, 1.5, 1.75 , 2 & 2.5 wt. % ) were fabricated by dispersing within an epoxy resin using a Ultrasound machine followed by mechanical stirring. The samples were heat treated at temperature ( 80 °C for 3 hrs) The mechanical properties of the composites were investigated. Wear and hardness properties measurements indicated higher wear rate and hardness with increasing concentration of MWCNTs . The MWCNTs significantly improved the wear resistance and hardness when compare than the pure epoxy. These note show too after heat treatment of composite with ( 80 oC for 3 hrs ).

تم تحضير متراكب نانومتري من مادة الايبوكسي مضاف اليه انابيب الكاربون النانوية متعدد الجدران وبنسب وزنية (0.25 ,0.5 , 1.75 , 1 , 1.25 , 1.5 , 1.75 , 2 , 2.5 ) % بتفريق داخل راتنج الإيبوكسي باستخدام جهاز الموجات فوق الصوتية متبوعاً بالتحريك الميكانيكي . العينات تعرضت لمعاملة في درجة حرارة (80 درجة مئوية ولمدة 3 ساعات) وتم التحقيق في الخواص الميكانيكية للمركبات . قياسات خصائص البلى والصلادة لمتراكب النانومتري أشارت إلى معدل أعلى للبلى والصلادة مع زيادة تركيز انابيب الكاربون النانوية . اضافة الكاربون النانوي ادى الى تحسين كبير في مقاومة البلى)التأكل ) والصلادة مقارنة بعينات الايبوكسي النقي . وكذلك تظهر بعد المعالجة الحرارية للعينات عند (80 درجة مئوية ولمدة 3 ساعات) . ER -