@Article{, title={Preparation of Tio2 nanoparticles by laser ablation in methanol solution}, author={Wisam J. Aziz وسام عزيز جعفر and Saja Q. Ali سجى قيس علي}, journal={Journal of College of Education مجلة كلية التربية}, volume={}, number={5}, pages={331-338}, year={2016}, abstract={In this work, Tio2 nanoparticles prepared by pulse laser ablation(PLA) of titanium target (purity of 99.99%) immersed in methanol solution by focused beam of 532 nm pulsed used Nd:YAG laser operating at different laser pulses in range (1000, 1500, 2000) pulses with 1Hz repetition rate, effective beam diameter 4.8 mm and 10 ns pulse width. Laser energy was kept constant at (900) mJ. The effects of methanol solution and number of laser pulses on the structural properties (XRD) and morphology (FESEM) was study. From XRD measurment have been revealed that 4peaks with 2θ values of 27.160, 36.2, 54.7 and 69.02 degree, corresponding to TiO2 crystal planes of (110), (101), (211) and (301) respectively at 2000 pulses in methanol solvent after heating at temperature 85 oC for 45 minute.

في هذا البحث تم تحضير الجسيمات النانوية من اوكسيد التيتانيوم Tio2 المحضر بواسطة الترسيب الفعال بالليزر النبضي بأستخدام ليزر ND:YAG الذي يعمل بطول موجي 532 نانو متر تم عملها بضربات ليزر مختلفة (2000,1500,1000) بأمد نبضة 10 نانو ثانيه وقطر حزمة 4.8mm كـوسيلة إقتلاع من سطح الهدف (التيتانيوم) ذو نقاوه 99.99% .تم دراسة تأثيرمحلول الميثانول وعدد ضربات الليزر على خصائص التركيبة و التشكيلية وبينت الدراسه من خلال قياسات الاشعة السينية وجود 4 قمم عند الزوايا 27.160=Ɵ 2 بالمستوى (110) , وقمة ايضآ عند الزاوية 36.2=Ɵ2 بالمستوى101) ) , وكذلك عند الزاويه =54.7Ɵ2 بالمستوى (211) وأخيرآ عند الزاوية 69.02=Ɵ2 بالمستوى (301) عند الشرط المثالي وهو 2000 ضربة بطاقة 900 بدرجة حرارة c˚ 85 لــ 45 ثانــيه.} }