@Article{, title={Using Lead as a Filler Material to Produce Porous Aluminum أستخدام الرصاص كمادة أملاء لانتاج الالمنيوم المسامي}, author={Salah Noori Alnomani and Essam Zuheir Fadhel}, journal={journal of kerbala university مجلة جامعة كربلاء}, volume={15}, number={2}, pages={225-234}, year={2017}, abstract={Porous materials are unique materials which can be used in light weight and strong structures. Few methods can be used to produce porous metals depending on the required degree of porosity, produced part size, nature of material and configuration. In this study, sintering technique was selected to produce porous aluminum using lead as a filler material. The whole process was conducted under vacuum environment at 500oC and different soaking time to investigate and select the proper environment parameters. Results show that soaking time impacts significantly the resulting porous aluminum. Two hours of sintering at 500oC and under vacuum environment was concluded as convenient parameters to produce controlled porous aluminum. The compacting process which used in producing green compacts was also investigated and it was found that 60MPa is the best selection of compacting pressure.

المواد المسامية هي مواد فريدة يمكن استخدامها في الهياكل القوية والخفيفة الوزن. هناك الكثير من الطرق التي يمكن استخدامها لإنتاج المواد مسامية اعتمادا على درجة المسامية المطلوبة، حجم القطعة المطلوب انتاجها، بالإضافة الى طبيعة المواد وتكوينها. في هذه الدراسة، تم استخدام تقنية التلبيد لإنتاج الألمنيوم المسامي باستخدام الرصاص كمادة وسيطة. أجريت العملية برمتها تحت بيئة تفريغ بدرجة حرارة تلبيد 500oC مستخدمين فترات زمنية مختلفة للتلبيد لغرض استقصاء معايير التلبيد المناسبة. بينت النتائج بأن زمن التلبيد المستخدم له تأثير واضح على الألمنيوم المسامي المنتج. وقد تبين بان التلبيد لمدة ساعتين بدرجة الحرارة المذكورة يعطي نتائج جيدة لأنتاج المنيوم مسامي مسيطر على نسبة مساميته. كما تم استقصاء قيمة الضغط المستخدم لكبس مسحوق المعدن وتبين أن استخدام قيمة ضغط 60MPa هو الأمثل في عملية كبس العينات} }