TY - JOUR ID - TI - Investigation on Mechanical Properties of Austenitic Stainless-Steel Pipes Welded by TIG Method AU - Mushtaq Albdiry PY - 2018 VL - 26 IS - 1 SP - 315 EP - 323 JO - Journal of University of Babylon مجلة جامعة بابل SN - 19920652 23128135 AB - This paper investigates the mechanical properties of austenitic stainless steel (type 204) pipes welded by Tungsten Inert Gas (TIG) welding process. Testing of hardness (HRC), tensile strength and bending strength was performed for the steel pipes welded at two different welding temperatures (700 °C and 900 °C) with and without using the weld filler wire. The microstructure of the welding regions was examined by using an optical microscopy. The properties showed that the steel pipes welded by 900 °C with using the weld filler obtained the highest tensile strength and bending strength versus these welded by 700 °C without the use of the weld filler. This is attributed to the weld filler heated and melt at sufficient temperature (900 °C) and compensate losing in the Ni metal occurred in the base steel metal during the welding process.

هذا البحث يدرس الخواص الميكانيكية للأنابيب الفولاذية الاوستنايتي (نوع 204) الملحومة بطريقة اللحام بغاز التنغستن الخامل. اجريت فحوصات اختبار الصلادة روكويل C، قوة الشد وقوة الانحناء لأنابيب الصلب الملحومة بدرجتين مختلفتين من درجة حرارة اللحام 700 درجة مئوية و900 درجة مئوية مع وبدون استخدام حشوة اللحام. كذلك تم إجراء فحص البنية المجهرية لمناطق اللحام. أظهرت الخصائص أن اللحامات الفولاذية المكتملة عند 900 درجة مئوية مع استخدام حشوة اللحام أعلى مقاومة شد ومقاومة انحناء مقارنة بتلك الملحومة بدرجة 700 بدون حشوة اللحام ويعزى ذلك الى ان حشوة اللحام انصهرت بدرجة حرارة كافية وقد ملئت النقص الحاصل لمعدن النيكل في المادة الاساس اثناء فترة اللحام. ER -