@Article{, title={Fabrication and Characterization of Chromium Nanotube Using (AAO) Template}, author={Rana Afif Anaee and Ahmed Rajih Hassan}, journal={Journal of University of Babylon مجلة جامعة بابل}, volume={26}, number={2}, pages={152-159}, year={2018}, abstract={In the current research, the fabricating of Cr nanotubes was done by electrochemical deposition in anodic aluminum oxide (AAO) as template. Characterization of fabricated Cr nanotubes were a achieved by XRD, SEM/EDS and TEM. These techniques indicated that the deposited chromium nanotubes have high purity within experimental conditions, the peaks in XRD was good agreement with JCPDS cards, SEM images showed the growth of ordered nanotubes in one plane perpendicular to the template (AAO). The purity of fabricating nanotubes was confirmed by EDS analysis, while the produced single walled nanotubes was shown from TEM images with open ends of tubes. 60 nm as diameter was obtained for fabricating Cr nanotubes.The fabrication of Cr nanotubes suggests producing quintuple bonds (Cr ≡ Cr) to form tubes without any chance to deposit chromium as particles.

في البحث الحالي تم تصنيع Cr Nanotube بعملية الترسيب الكهروكيميائي وذلك بترسيبها على أساس من الألمنيوم المؤنود AAO كذلك تم تشخيص الأنابيب الكروم النانوية بواسطة XRD, SEM/EDS and TEM . وقد تبين من خلال هذه التقنيات إن الأنابيب الكروم النانوية كانت تمتلك نقاوة عالية جدا , ومن خلال تقنية SEM لوحظ نمو منتظم للأنابيب النانوية على مستوى عمودي للـ AAO. وكذلك يتضح ذلك من خلال تقنية TEM والتي يظهر فيها الأنابيب ذات جدار منفرد single wall بقطر مقارب إلى 60nm.} }