TY - JOUR ID - TI - INVESTIGATION SOME PROPERTIES OF (ZN-NI-SIC) COMPOSITES COATING ON LOW CARBON STEEL تحري بعض خواص طبقة الطلاء (Zn-Ni-SiC) المترسبة على نماذج من الفولاذ واطئ الكاربون AU - Abdalwahid K. Rajih Jaleel K. Ahmed Nabaa S. Radhi عبد الواحد كاظم راجح جليل كريم أحمد نبأ ستار راضي PY - 2018 VL - 18 IS - 2 SP - 393 EP - 374 JO - Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد SN - 20761819 AB - This work represents an attempt to introduce further improvement on the properties of these coatings, although the (Zn-Ni) deposition is known to be an anomalous electrodeposited process , where added Ceramic materials is (silicon carbide) ,with very good mechanical properties.Carbon steel samples were coated with (Zn-Ni) and (Zn-Ni-SiC) particles with different particles size of silicon carbide once microscale (73µm) and another nanoscale (70-100nm) .After electroplating, these samples were analyzed by X-ray fluorescent to confirm all the content for each alloy.

يهدف هذا البحث لادخال تحسينات إضافية على خواص طبقة الطلاء (Zn-Ni) ، حيث تم أضافة مادة سيراميكية هي كاربيد السيليكون التي تمتاز كمثيلاتها من المواد السيراميكية بخواصها الميكانيكية الجيدة . تتضمن هذه الدراسة التحري عن بعض خواص طلاء (Zn-Ni) بعد اضافة مادة كاربيد السيليكون بحجميها المايكروي (≈73µm) والنانوي(70-100nm) المترسبة على نماذج من الفولاذ منخفض الكاربون.تضمنت الخواص المدروسة كلا من اختبار فلورة الاشعة السينية والخشونة والمسامية واختبار الصدمة الحرارية وقد ظهر تطابق بين نتائج اختبار المسامية والخشونة حيث إن هنالك علاقة بينهما إذ ان الخشونة العالية تسبب مسامية عالية وبذلك يكون تسلسل المسامية والخشونة الموجودة في طبقة الطلاء كالاتي: (Zn-Ni) >(Zn-Ni-nSiC) >(Zn-Ni-mSiC). كما أظهرت طبقة الطلاء (Zn-Ni-nSiC) نتائج جيدة في إختبار الصدمة الحرارية. ER -