TY - JOUR ID - TI - Preparation of SnO2 thin films and study of some of their electrical properties at different substrate and annealing temperatures. تحضير ودراسة بعض الخواص الكهربائية لأغشية SnO2عند درجات حرارة ترسيب وتلدين مختلفة AU - Saeed. N.Turkey AU - Raad S. Sabri رعد سعدون صبري PY - 2009 VL - 3 IS - 1 SP - 91 EP - 94 JO - Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة SN - 19918941 27066703 AB - Abstract:Thin film of SnO2 were prepared by thermal chemical spray deposition technique at differentsubstrate temperatures ( 350 ,450 ,550 ) °C and prepared samples were annealed for 30 minutes at differentannealing temperatures ( 300,400) °C . the D.C conductivity was studied , and there were two activationenergies for the prepared films , and also two mechanisms of conductivity , first at low temperatures andthe second at high temperatures. The activation energies looked to be increased at annealing temperature 200°C and decreased at annealing temperature 300 °C.

: في هذا البحث تم تحضير أغشية SnO2 الرقيقة بطريقة الرش الكيميائي الحراري والمرسبة على قواعد زجاجية وبدرجات حرارة قاعدة مختلفة ( 350,450,550 °C) ، وتلدين تلك الأغشية لمدة min 30 وبدرجات حرارة °C ( 300,400 ) ودرست التوصيلية الكهربائية المستمرة وحساب طاقة التنشيط لتلك الأغشية وقد وجد إن هناك ميكانيكيتان للتوصيل ولكافة الأغشية الأولى عند درجات الحرارة الواطئة والثانية عند درجات الحرارة العالية وان طاقة التنشيط تزداد مع زيادة درجة حرارة القاعدة وأنها تزداد بالتلدين بدرجة حرارة °C 200 وتنخفض عند التلدين بدرجة °C 300 . ER -