TY - JOUR ID - TI - Effect of α-TeO2 Substitution on Hg- System Properties AU - Shatha H. Mahdi PY - 2018 VL - 29 IS - 2 SP - 169 EP - 174 JO - Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية SN - 1814635X 25213520 AB - Specimens of HgBa2-xTexCa2Cu3 O8+ with x =0, 0.15, 0.3 and 0.45, were prepared by traditional method (SSR). The results showed enhancing structural and electrical (resistivity vs temperature) properties, where XRD analysis shows a tetragonal structure for all specimens and high ratio of Hg-1223 phase with an increase of the lattice parameter and Tc, except x=0.45, it shown semiconductor. The HgBa1.70Te0.30Ca2Cu3 O8+ specimen with x= 0.3 shows the highest (Tc=143K) than with Tc of the basic compound HgBa2Ca2Cu3 O8+ equal (135K), at increment of Te content. While mechanical properties have been weakened as consequence to increasing brittleness of HgBa2-xTexCa2Cu3 O8+ compounds at increment Te content

تم تحضير العينات HgBa2-xTexCa2Cu3 O8+ بالطريقة التقليدية (تفاعل الحالة الصلبة SSR). اظهرت النتائج تحسن الخواص التركيبية و الكهربائية (تغير المقاومية مع درجة الحرارة)، حيث اظهرت نتائج حيود الاشعة السينية ان التركيب السائد هو الرباعي لكل النسب ماعدا نسبة 0.45 فإنه يظهر تركيب شبه موصل. تبين العينة HgBa1.70Te0.30Ca2Cu3 O8+( x=0.3 ) لها اعلى انتقال (Tc=143K) مقارنة مع المركب الاساس HgBa2Ca2Cu3 O8+ (135K) عند زيادة محتوى Te.بينما ضعفت الخصائص الميكانيكية لمركب HgBa2-xTexCa2Cu3 O8+ نتيجة ازدياد الهشاشة مع زيادة محتوى Te . ER -