TY - JOUR ID - TI - Doping effect by SiO2 on optical properties of ZnO Thin Films Prepared by pulsed laser depositions (PLD) technique تأثير التشويب بأوكسيد السيليكون على الخواص البصرية للأغشية أوكسيد الخارصين الرقيقة المحضرة بتقنية الترسيب بالليزر النبضي AU - Zuheer. N. Majeed1 زهير ناجي مجيد1 AU - Abdul-Majeed E. Al-Samarai1 عبد المجيد عيادة السامرائي1 AU - Ghuson. H.Mohammed2 غصون حميد محمد2 PY - 2019 VL - 24 IS - 1 SP - 93 EP - 97 JO - Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة SN - 18131662 24151726 AB - In this paper,Zinc oxide was dopped by various concentrations (5,10,15,20,25) % wt, silicon oxide The mixture was deposited on glass substrate by laser pulse deposition at room temperature to obtain (Zn2SiO4) thin films .The optical properties of thin films prepared on spectral absorption and transmission recording were studied at the wavelength range (200- 1100) nm. Some of the optical constants, including absorptance, transmission, absorption coefficient, and energy gap are calculated before and after annealing at (400 ̊C) for (1 hr). Absorptance values and absorption coefficient increase after doping and transmission and energy gap decreases after the doping. Absorbance values and absorption coefficient decreases after annealing and transmission and energy gap increase after the annealing .

في هذا البحث تم تشويب اوكسيد الخارصين بنسب تراكيز (25,20,15,10,5) % من اوكسيد السيليكون ورسب الخليط على ارضيات زجاجية بتقنية الترسيب بالليزر النبضي وفي درجة حرارة الغرفة للحصول على اغشية سليكات الخارصين. تمت دراسة الخواص البصرية للاغشية المحضرة من خلال طيف الامتصاصية والنفاذية ضمن مدى الاطوال الموجية nm (200-1000). تم حساب بعض الخواص البصرية ومنها الامتصاصية والنفاذية ومعامل الامتصاص وفجوة الطاقة قبل وبعد التلدين لمدة ساعة واحدة وبدرجة حرارة (400C ͦ). أظهرت النتائج زيادة في الامتصاصية ومعامل الامتصاص بعد التشويب ونقصان النفاذية وفجوة الطاقة بعد التشويب. أظهرت النتائج نقصان الامتصاصية ومعامل الامتصاص بعد التلدين وزيادة النفاذية وفجوة الطاقة بعد التلدين. ER -