TY - JOUR ID - TI - Effect of Titanium Carbide Particles on Mechanical Properties of Aluminum Matrix Composites تأثير حبيبات كاربيد التيتانيوم على بعض الخواص الميكانيكيه لمادة متراكبة ذات اساس المنيوم AU - Zaman Khalil Ibrahim زمن خالد ابراهيم PY - 2017 VL - 5 IS - 2 SP - 20 EP - 30 JO - Wasit Journal of Engineering Sciences مجلة واسط للعلوم الهندسية SN - 23056932 AB - In this research aluminum matrix composites (AMCs) was reinforced by titanium carbide (TiC) particles and was produced. Powder metallurgy technique (PM) has been used to fabricate AMCs reinforced with various amounts (0%, 4%, 8%, 12%, 16% and 20% volume fraction) of TiC particles to study the effect of different volumefractions on mechanical properties of the Al-TiC composites.Measurements of compression strength and hardness showed that mechanical properties of composites increased with an increase in volume fraction of TiC Particles.Al-20 % vol. TiC composites exhibited the best properties with hardness value (97HRB) and compression strengthvalue (275Mpa)

.تم في هذا البحث انتاج مادة متراكبة ذات اساس المنيوم مدعم بكاربيد التيتانيوم .تقنيه ميتالوجيا المساحيق استعملت في تصنيع المادةالمركبةالتي اساسها الالمنيوم المدعمةبنسب حجميه مختلفةتتراوح%,8%, 12%, 16% and 20%)4(0%,من ماده التقويةكاربيد التيتانيوم لدراسةتأثيرهذه النسب الحجميةالمختلفةعلى الخواص الميكانيكيةللمادةالجديدة.تم فحص الخواص الميكانيكية(قوه الانضغاط والصلادة) وحصلنا على النتائج , وبصوره عامه وجدنا أن الخواص الميكانيكيةتزداد مع زياده النسب الحجميةلحبيبات كاربيد التيتانيوم.وكانت أفضل خواص ميكانيكيه لعينات المواد المتراكبة+20%TiC)Al%80) مقارنه بعينات الالمنيوم غير المدعم حيث كانت اعلى زياده بقيمه الصلادة(97HRB) وقوه الانضغاطMpa) 275. ) ER -