TY - JOUR ID - TI - Using of Carbon Fibers in Strengthening Polymer Concrete استخدام الياف الكاربون في تقوية الخرسانه البوليمريه AU - Sabah Ageeb Kassid صباح عجيب كاصد AU - Hameed Rasheed Hommadi حميد رشيد حمادي AU - Khalid Mahdi Thajeel خالد مهدي ثجيل AU - Abdul Majeed Hassan Abdul Majeed عبد المجيد حسن عبد المجيد PY - 2014 VL - 5 IS - 2 SP - 72 EP - 78 JO - Iraqi Journal of Science and Technology المجلة العراقية للعلوم والتكنولوجيا SN - 18136893 29584604 AB - The mechanical behavior of polymer concrete reinforced with chopped carbon fibers have been studied in terms of tensile strength ، flexural strength ، compressive strength and young's modulus . Unsaturated polyester resin was used as a binder at weight fraction 30% ، with three types of fillers silica 20% with particle size 399 µm ، sand 38-40% with sizes 125-212 m and fine stone 7-10% with sizes 1.4-2.4 mm ، while the weight fraction of chopped carbon fibers was up to 5% with length 6.5 mm and diameter is 0.12mm which added as randomly and in different orientations .The results from this study show that the addition of carbon fibers leads to improve the mechanical properties of polymer concrete

درست التصرف الميكانيكي لخرسانه بوليمريه مقواة بالياف الكاربون المقطعّة بدلالة مقاومة الشد ومقاومة الحني ومقاومة الكبس ومعامل المرونه . حيث استخدم البولي استر غير المشبع كمادة بوليمرية رابطه وبنسبة وزنية 30% واستخدمت ثلاثة انواع من المالئات هي السليكا بحجم 399 مايكرون وبنسبة وزنية 20% والرمل بحجم 125-212 مايكرون وبنسبة وزنية 38- 40% وحصى ناعم بحجم 1.4- 2.4ملم وبنسبة7-10% اما نسبة الياف الكاربون فكانت1-5% وباطوال متساوية 6.5 ملم وبقطر 0.12 ملم ، وقد اضيفت الالياف بشكل عشوائي بالنسبة للاتجاهات .وتبين من نتائج هذه الدراسة، ان اضافة الياف الكاربون ادى الى تحسين الخواص الميكانيكية للخرسانه البوليميريه بشكل ملحوظ ER -