TY - JOUR ID - TI - Synthesis and Characterization of Gold Nanoparticles by Aluminum as a Reducing Agent تحضير وتشخيص جسيمات الذهب النانوية باستخدام الالمنيوم كعامل مختزل AU - Muna Ahmed Saeed منى احمد سعيد AU - Dhelal Abdul Ghafoor ظلال عبد الغفور AU - Mazin K. Hamid مازن كامل حامد AU - Rana M. Yas رنا محي ياس PY - 2020 VL - 17 IS - 1 Supplement SP - 336 EP - 341 JO - Baghdad Science Journal مجلة بغداد للعلوم SN - 20788665 24117986 AB - The synthesis of nanoparticles (GNPs) from the reduction of HAuCl4 .3H2O by aluminum metal was obtained in aqueous solution with the use of Arabic gum as a stabilizing agent. The GNPs were characterized by TEM, AFM and Zeta potential spectroscopy. The reduction process was monitored over time by measuring ultraviolet spectra at a range of λ 520-525 nm. Also the color changes from yellow to ruby red, shape and size of GNP was studied by TEM. Shape was spherical and the size of particles was (12-17.5) nm. The best results were obtained at pH 6.

تحضير جسيمات الذهب النانوية عن طريق اختزال ايون الذهب الموجود في حامض HAuCl4.3H2O الاوريك بواسطة استخدام الالمنيوم كعامل مختزل اجري التفاعل في محلول مائي مع استخدام قطع من الصمغ العربي كعامل مثبت (عامل استقرار) لجسيمات النانو , ثم تم تشخيص الجسيمات المتكونة بواسطة كل من التقنيات التالية, المجهر الالكتروني النافذ, مجهر القوة الذرية, وجهد زيتا , عملية الاختزال تمت مراقبتها عن طريق تغير طيف الاشعة فوق البنفسجية مع الوقت وكان معدل الطول الموجي لاعلى قمة بين 520- 525نانومتر وكذلك مراقبة اللون اثناء تغيره من الأصفر الى الأحمر حيث يشير الى تكون الجسيمات النانوية و شكل وحجم الجسيمات تمت دراستهما من خلال صور المجهر الالكتروني النافذ حيث كان شكل الجسيمات كروي وحجمها بين 12-17.5 نانومتر. وان افضل النتائج كانت في مقياس حموضة (الاس الهيدروجيني) 6 . ER -