@Article{, title={Deposition of Iron Oxide Thin Films by Spray Pyrolysis Method ترسب الأفلام الرقيقة (أكسيد الحديد) عن طريق رذاذ الانحلال الحراري باستخدام مركبات فيروم مختلفة}, author={Sanaa Rafat Yaseen سناء رفعت ياسين}, journal={Academic Science Journal مجلة العلوم الاكاديمية}, volume={18}, number={03}, pages={50-65}, year={2022}, abstract={The growth and characterization of iron oxide thin films by spray pyrolysis method using iron chloride hexahydrate. Iron oxide films deposited on well cleaned glass substrate at different substrate temperatures varying from 2500C to 5000C in air atmosphere. The characterization of iron oxides films was investigated for their optical and morphological properties by using spectroscopy and Scanning Electron Microscopy. The atomic absorption spectroscopy showed the existence of direct band gap energy nearly 2.18 eV with varying substrate temperature. Optical, structural and morphological observations were showed the film quality was getting better at 350 0C substrate temperature, also grain sizes were cleared.

أودعت هذه الدراسة أفلام أكسيد الحديد عن طريق رذاذ الانحلال الحراري في ظل ظروف ترسب مختلفة. تم التحقيق في تأثير تقنية التحضير على الخصائص الهيكلية والبصرية لأفلام Fe2O3 أكسيد الحديد باستخدام حيود الأشعة السينية (XRD). تم إعداد أفلام أكسيد الحديد Fe2O3 عن طريق تقنية الانحلال الحراري الرش في درجات حرارة الركيزة المختلفة، وذلك باستخدام FeCl3.6H2O ، FeCl3.4H2O ، و FeSO4.7H2O (0.1M). ودرست بنية الكريستال من الأفلام من قبل حيود الأشعة السينية كما درس أن هناك قمم الحيود موجودة مع قيم 2а; 38.523، 44.77، 65.16، 78.297 في درجات، المقابلة للطائرات الكريستال من (320)، (410)، (200)، (444) من أكسيد الحديد البلوري والحديد لكل درجة حرارة الركيزة، على التوالي. جميع الأفلام درجة حرارة الركيزة تظهر نفس الهياكل الكريستال. يتغير مستوى البلورة وفقا لدرجة حرارة الركيزة؛ وقد لوحظ أفضل بلورة في درجة حرارة الركيزة 350 درجة مئوية. أفلام أكسيد الحديد رش المودعة في الركيزة.} }