TY - JOUR ID - TI - Some Properties of High Performance Carbon Fibres Cement Composites بعض خواص الخرسانة عالية الأداء المسلحة بألياف الكاربون AU - Nada Al – Jalawi PY - 2009 VL - 15 IS - 4 SP - 4409 EP - 4416 JO - Journal of Engineering مجلة الهندسة SN - 17264073 25203339 AB - The paper presents properties of high performance concrete reinforced with relatively high percentage of choped carbon fibers vol. fraction ranging from (1 to 5) %. The great advantage of such composites is their relatively high flexural strength. A low water to cement ratio of 0.3 with super plasticizer was used in order to keep the cement mix easily workable. To improve the properties, a locally existing pozzolan based on reactive meta- kaolin was used in the mixture together with silica sand. A high modulus carbon fibers (450 KN/mm2) were also used. In addition to the flexural strength, dynamic modulus of elastisity were found using dynamic methods. The results showed that the specimen failed in flexureal by a single crack although the ultimate tensile strength and the stiffness of the composite were increased as the fibers content was increased.

يقدم البحث خواص الخرسانة العالية الأداء المسلحة بألياف الكاربون بنسب حجمية عالية نسبياً تتراوح من (1 – 5) % . إن الفائدة الكبيرة لهذا النوع من الخرسانة هي مقاومتها العالية للشد في الانحناء.تم استخدام نسبة واطئة من الماء/السمنت تساوي (0.3) مع استخدام ملدن متفوق للحصول على قابلية تشغيل مقبولة كما تم استخدام بوزلان محلي متكون من دقيق الكاؤولين النشط واستخدام رمل ذو أساس سيليكي وكانت ألياف الكاربون من نوع ذات معامل المرونة العالية (450 كيلونت/ملم2), بلإضافة إلى الخواص الانحنائية فقد تم بحث الخواص الديناميكية باستخدام طرق ديناميكية, وبينت النتائج بأن نوع فشل النماذج كانت بشق منفرد (single crack) وأن كلاً من مقاومة الانثناء القصوى ومعامل المرونة تزداد بزيادة نسبة الألياف. ER -