TY - JOUR ID - TI - Preparation of barium ferrite BaFe12O19 and the study of the effect of fast neutrons on its magnetic and dielectrical properties. تحضير الباريوم فرايت BaFe12O19 ودراسة تأثير النيوترونات السريعة على خواصه المغناطيسية والكهربائية AU - Dr. Jassim Mohammed Yaseen م.د.جاسم محمد ياسين PY - 2011 VL - 11 IS - 1 SP - 633 EP - 640 JO - College Of Basic Education Researches Journal مجلة ابحاث كلية التربية الاساسية SN - 19927452 AB - Hard hexagonal barium ferrite BaFe12O19 was prepared by solid state reaction method using a precursor (BaO- 6 Fe2O3 (mixture at calcinations temperature 1100 C for 2 hr. The XRD patterns of the calcined samples show the formation of BaFe12O19 at this temperature .In this work, some of the samples were irradiated by fast neutron (241Am-Be ) in average energy 5 MeV with flux ( 1.5 ×106 n/cm2.s ). The fast neutron irradiation did not affect the magnetic properties of prepared samples obviously, but it affected the electrical resistivity in direct relation in which the increasing of irradiation dosages lead to increasing of electrical resistivity obviously .

تم تحضير مادة الباريوم فرايت BaFe12O19 بطريقة التفاعل الصلب عن طريق خلط المركبين BaO وFe2O3 بالنسبة المولية (BaO- 6 Fe2O3) . بعد اجراء عمليات الخلط الرطب والتجفيف تم حرق الخليط بدرجة حرارة 1100 C ولمدة ساعتين . باستخدام تقنية الحيود للاشعة السينية تم الحصول على نموذج الحيود السيني لطور الباريوم فرايت BaFe12O19 المحضر وفق الظروف أعلاه. في هذا العمل تم تشعيع بعض النماذج بالنيوترونات السريعة (241Am-Be ) وبمعدل طافي قدره5 MeV وبفيض نيوتروني قدره (( 1.5 ×106 n/cm2.s نتائج التشعيع أظهرت أن التشعيع النيوتروني وفق الظروف اعلاه لم يؤثر على الخواص المغناطيسية للباريوم فرايت بشكل واضح , في حين أثرت بشكل كبير على المقاومية الكهربائية للمادة , حيث أن المقاومية الكهربائية تزداد بزيادة الجرعة الإشعاعية . ER -