TY - JOUR ID - TI - Effect of Recycling on Rheological and Mechanical Properties of High Impact Polystyrene تأثير عمليات إعادة التصنيع على خواص الانسياب و الخواص الميكانيكية لمادة البولي ستايرين المقاوم للصدم AU - Sawsan D. A. Shubbar سوسن ضياء احمد شبر PY - 2010 VL - 2 IS - 2 SP - 103 EP - 114 JO - KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية SN - 20715528 25230018 AB - High impact polystyrene (HIPS) was subjected to repeated thermal and shear stresses by different methods, using a high pressure capillary Rheometer, a laboratory extruder and a Brabender plasticorder. The results showed that the recycling of HIPS caused a decrease in the shear stresses and consequently in the viscosity at constant shear rate. The high pressure capillary Rheometer gave a greater decrease than with the Brabender plasticorder. Tensile strength values were progressively decreased with the laboratory extruder, but increased in the case of Brabender mixer; the elongation was decreased in both cases. This work was then applied in a local plant to compare experimental and actual results.

تم تعريض مادة البولي ستايرين المقاوم للصدم إلى اجهادات حرارية و قوى قص بعدة وسائط و طرق تشمل استخدام جهاز الريوميتر الشعري ذو الضغط العالي و جهاز البثق ألمختبري و جهاز خلط المعاجين البوليمريه. حيث أوضحت النتائج أن إعادة التصنيع لمادة البولي ستايرين المقاوم للصدم عن طريق إعادة صهرها و تشكيلها تسبب انخفاضا في اجهادات القص و بالتالي هناك انخفاض في اللزوجة أيضا بثبوت معدلات القص. كما لوحظ أن معدل الانخفاض في اللزوجة عند استعمال جهاز الريوميتر الشعري أعلى من مثيله عند استعمال جهاز البثق ألمختبري ؛ أما في حالة استعمال جهاز خلط المعاجين البوليمريه فقد زادت متانة الشد ولوحظ حصول تناقص في قيمة الاستطالة عند إعادة صهرها و تشكيلها بكلا الجهازين الأخيرين. من ثم تم تطبيق هذا العمل المختبري في احد المعامل المحلية لغرض مقارنة النتائج المستحصله. ER -