TY - JOUR ID - TI - FAILURE STRENGTH OF FABRIC COMPOSITES WITH DRILLED AND MOULDED-IN HOLES إجهاد الكسر لحصائر المواد المركبة المثقوبة قبل وبعد الصب AU - Ehsan Sabah M. Al-Ameen احسان صباح محمد الأمين PY - 2011 VL - 4 IS - 2 SP - 1 EP - 8 JO - Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية SN - 19984456 24117773 AB - The effect of drilled and moulded-in circular holes of woven fabric composites on failure strength have been examined in flexural test. Three types of woven fabric-reinforced composite systems were used: glass fiber (E glass), Kevlar fiber, and glass- Kevlar hybrid in polyester matrix. All these types are of (30%) volume fraction, and hole diameter of (1, 2, 3, 4 and 5 mm) for each type. ISO standard flexural specimens were tested and repeated three times.It is noticed that the specimens with moulded-in holes exhibit failure strengths higher than those of drilled specimens by (7- 24%). Also the values of stress concentration factors (Kt) increase with increasing the hole size for all types of laminates, and they were arranged in an ascending order as follows: Kevlar/ polyester, glass-kevlar hybrid/ polyester, and glass/ polyester.

في هذا البحث تم دراسة تأثير قطر الثقوب قبل الصب وبعد الصب على إجهاد الكسر لحصائر المواد المركبة بتسليط أحمال انحناء عليها0 تم استخدام ثلاثة أنواع من المواد المركبة المقواة بالالياف وهي الالياف الزجاجية (نوع E)، الياف الكفلر ومادة هجينة من الالياف الزجاجية والياف الكفلر في راتنج البوليستر وبنسبة كسر حجمي مقداره (30%)، وبقطر ثقب ( 1, 2, 3, 4 و5 ملم) لكل نوع، حيث استخدمت المواصفات العالمية (ISO Standard) لاختبار الانحناء وتحضير العينات وإجراء الاختباروالتكرار لثلاث مرات.لوحظ أن قيم اجهاد الكسر للعينات المثقوبة قبل الصب اعلى مقارنة بالعينات المثقوبة بعد الصب بمقدار (7-24%). كذلك فأن قيم معاملات تركز الاجهاد تزداد بزيادة قطر الثقوب لجميع الانواع، وان قيمها مرتبة تصاعديا كمايلي: الياف الكفلر، الالياف الهجينة من الكفلر والالياف الزجاجية واخيراً الالياف الزجاجية في راتنج البوليستر0 ER -