TY - JOUR ID - TI - The Effect of Shot Peening and Residual Stresses on Cumulative Fatigue Damage تأثیر القذف بالكرات والاجھادات المتبقیة على ضرر الكلال التراكمي AU - Hussain J. M. Alalkawi AU - Qusay Khalid Mohammed AU - Waleed Sadun Al-Nuami PY - 2010 VL - 28 IS - 15 SP - 5055 EP - 5070 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - A series of constant and cumulative fatigue tests under the effect of shot peening were conducted for two aluminum alloys 2024 and 5052. Three unpeed specimens were tested for each alloy under low-high stress levels (120-280 MPa) for 2024 aluminum alloy and (40-90 MPa) for 5052 aluminum alloy at room temperature and stress ratio R= -1. Other specimens were exposed to shot peening with different blasting time before the cumulative fatigue testing. It is found for 2024 Al alloy that as the shot peening time increases the cumulative fatigue life is improved but above 10 min. the life is reduced. For 5052 Al alloy the cumulative fatigue life is reduced as shot peening time increases

تم إجراء مجامیع من فحوصات الكلال ثابتة ومتغیرة السعة تحت تأثیر القذف بالكریات المعدنیة لسبیكتین من الألمنیوم 2024 و 5052 . تم فحص ثلاثة عینات غیر مقذوفة لكل سبیكة تحت مستویات 40-90 ) لسبیكة 5052 تحت درجة MPa) 120-280 ) لسبیكة 2024 و MPa) إجھاد واطيء- عالي فحصت العینات الباقیة بأزمان مختلفة من القذف قبل فحص . R= - حرارة الغرفة ونسبة إجھاد 1الكلال التراكمي .بینت النتائج انھ كلما زاد زمن القذف تحسن عمر الكلال التراكمي و للسبیكة 2024 لكن عند أعلى من 10 دقائق فأن العمر سیقل بینما لسبیكة 5052 فأن عمر الكلال التراكمي یقل كلما زاد زمن القذف ER -