TY - JOUR ID - TI - The Effect of CNT Doping on the Hydrogenation Behavior of Y5Si3 Phases AU - Mouaid A. Hassen مؤيد علي حسن AU - Maher Khalid Ali ماهر خالد علي AU - Salah Suaod Al-Eissa صلاح سعود العيسى PY - 2012 VL - IS - 45 SP - 45 EP - 53 JO - Iraqi National Journal Of Chemistry المجلة العراقية الوطنية لعلوم الكيمياء SN - 22236686 AB - Abstract The reactivity of the CNT-doped Y5Si3 compared to Y5Si3 phase system has been investigated. Both alloys have been prepared by arc melting and their reactivity with hydrogen has been studied. Single–phase CNT-doped Y5Si¬3 can only be made by melting preformed Y5Si¬3 with the CNT. An activation process has been developed to induce reaction of the doped alloy with hydrogen. It involves cycling in H2 gas pressures above 1.2 atm at temperature higher than 435oC depending on the CNT content. Conditioned samples, will repeatedly (above 50 cycles) cycles 2.5 H (fu)-1 between room temperature and 500oC with 0.9 and 1.2 H (fu)-1 being desorbed and absorbed with fast kinetic within a very small temperature range. This behavior is believed to arise from the polymorphic change between an α-form of the D88 structure and a supercell β-form. An attempt to quantify the enhanced stability, compared to Y5Si3, is made by measuring reaction enthalpies using Van’t Hoff isopleths.

الخلاصة قورنت فعالية انبوب الكاربون النانو CNT المعالج بالسبيكة Y5Si3 مع السبيكة Y5Si3 وتم التحقق منها‚ ان كلا السبيكتين حضرت من صهرهم بالقوس ودرست فعاليتهم مع الهيدروجين∙ الطور الاحادي لسبيكة انبوب الكاربون النانوCNT المعالج بالسبيكة 3Y5Si يمكن فقط تصنيعها بالانصهار حتي تشكل السبيكة الجديدة من 3Y5Si مع انبوب الكاربون النانو CNT ∙ان عملية التنشيط تم تطويرها لاستمالة التفاعل مع السبيكة المعالجة باتجاه الهيدروجين ويتضمن تحولق في غاز الهيدروجين عند ضغط فوق 1,2 جو ودرجة حرارة اعلي من 435 سليزية اعتمادا علي المحتوی من انبوب الكاربون النانو NT C ∙ ER -