TY - JOUR ID - TI - Effect Of The Polymeric Structure On Activity Activated Carbon تأثير تركيب المواد البوليمرية على فعالية الكاربون المنشط AU - A. N. Al-Halauajy PY - 2011 VL - 16 IS - 3 SP - 136 EP - 140 JO - Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة SN - 18131662 24151726 AB - In this word, The activated carbon was prepared using waste polymers (rubbers, melamine and novolac) as raw materials. First carbonized was conduced at 350 °C for 3 hrs. The carbonized materials was activated by impregnation in 5% solution of zinc chloride for different periods of time at room temperature. The purified samples obtained from various experiments were evaluated by measuring the ability of active carbon to the adsorption of methylene blue and iodine. Moreover, density, humidity and ash content were measured and compared with the commercial sample.

نظراً لاكتساب الكاربون المنشط اهمية كبيرة في مجالات صناعية عدة فقد ركز الباحثون على انتاج انواع مختلفة من الكاربون المنشط من مصادر مختلفة وبطرائق متنوعة، وفي دراستنا هذه تم تحضير الكاربون المنشط من مخلفات بوليمرية ملوثة بيئياً بهدف ايجاد منفذ سليم لاستغلالها بشكل نافع وتخليص البيئة من مضارها الصحية والبيئية. تم كربنة المواد البوليمرية عند 350 °م لمدة ثلاث ساعات وحددت مواصفات المادة الكاربونية الناتجة عن طريق قياس بعض الخواص الفيزيائية. المادة الكاربونية السابقة شخصت كيميائياً باستخدام اسلوب النقع بمحلول 5% وزناً من كلوريد الخارصين وبأزمان مختلفة عند درجة حرارة المختبر، بعد ذلك رشحت المادة الكاربونية وحددت مواصفاتها الفيزيائية وقورنت مع النموذج التجاري. ER -