TY - JOUR ID - TI - Anodic Polarization of Anodized Aluminum Alloy 5052 AU - Ala’a Mishgel Ali AL-Asade علاء مشجل AU - Aparel S. Yaro ابرائيل سركيس يارو PY - 2009 VL - 10 IS - 2 SP - 1 EP - 8 JO - Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط SN - 19974884 26180707 AB - Aluminum alloy 5052 had been anodized by sulfuric acid as an electrolyte under constant voltage and the anodic oxide film produce will be testing by potentiostatic anodic polarization .Two variables, which were considered as important variables, were studied. These variables are anodizing time 15,30 min. and sealing time 10,20 min., and the test by potentiostatic anodic polarization through electro chemical polarization measurements in solutions of 1N na2so4 ( PH= 1 ). The results are discussed in light of the rate of ionic current flow through the coating during anodic polarization measurements.

الهدف من هذا العمل هو دراسة الطبقة الاوكسيدية المتكونة على سبيكة الالمنيوم 5052 بواسطة حامض الكبريتيك كمحلول الكتروليتي تحت تأثير فولتية ثابتة ,تركيز المحلول الالكتروليتي:15% كنسبة حجمية من حامض الكبريتيك ,درجة الحرارة:45 °م ,كثافة التيار:1.4 امبير/دسم2 ,زمن الانودة:30.15 دقيقة ,زمن الختم:20.10 دقيقة و الطبقة الاوكسيدية الناتجة يتم اختبارها بواسطة تقنية الاستقطاب الانودي ذو الجهد الثابت يقاس من خلال المحلول الالكتروليتي (PH=1) 1N Na2SO4 ان معدل نمو او تعاظم سبيكة الالمنيوم هو مظهر مهم في تخمين كفاءة عملية الانودة .في هذا العمل معدل نمو سبيكة الالمنيوم 5052 تمت دراستها مع تغير العوامل :زمن الانودة ,سمك الطبقة المتكونة وزمن ختم النموذج المؤنود.النتائج العملية اظهرت:1.ان معدل نمو سبيكة الالمنيوم بصورة عامة ازدادت نوعياً بزيادة زمن الانودة.2.عملية الاستقطاب الانودي الساكن للطبقة المؤنودة على سطح الالمنيوم كانت حساسة وتتأثر بكل من:سمك الطبقة و درجة الختم.3.ان سمك الطبقة المتكونة من عملية الانودة الاكثر سمكاً و اطول زمناً ختماً بصورة عامة تسمح بمرور اقل تيارات موجبة. ER -