TY - JOUR ID - TI - Warm Forming of Aluminum Alloy 2024 at Different Temperatures التشكيل الدافئ لسبيكة الألمنيوم (2024) عند درجات حرارة مختلفة AU - O. Th. Jumah عمر ذنون جمعة AU - W. J. Ali وليد جلال علي PY - 2012 VL - 20 IS - 2 SP - 78 EP - 85 JO - AL-Rafidain Engineering Journal (AREJ) مجلة هندسة الرافدين SN - 18130526 22201270 AB - AbstractForming of aluminum sheets at warm forming temperatures has been investigated as an alternative manufacturing process for improving formability compared with forming at room temperature. However, the forming technology should be developed to increase the application field, especially in the predication of formability and the failure in order to design the process and die outcomes. The results obtained during this study showed that the formability of annealed Al-alloy (Al-2024-O) is increased by increasing temperature. Its formability is significantly improved compared with the precipitation hardened alloy (Al-2024-T3). The possibility of forming (Al-2024-T3) sheet metal at moderate temperatures, with acceptable formability and higher strength for structural parts is much better if compared to the annealed condition (Al-2024-O).Key words : warm forming, formability, aluminum alloy (2024)

الخلاصةتم دراسة تشكيل صفائح الألمنيوم عند درجات حرارة التشكيل الدافئ كطريقة بديلة في التصنيع من اجل تحسين قابلية التشكيل مقارنة بالتشكيل عند درجة حرارة الغرفة. على أية حال فان تكنولوجيا التشكيل يجب إن تطور لزيادة تطبيقها وخصوصا في التنبؤ بقابلية التشكيل والفشل من اجل تصميم عملية التشكيل والمعدات الخاصة بها. أظهرت النتائج خلال هذه الدراسة بان قابلية التشكيل لسبيكة الألمنيوم (AL-2024-O) في ظرف التلدين التام تزداد بازدياد درجة الحرارة وإنها تظهر تحسن واضح مقارنة بسبيكة الألمنيوم (Al-2024-T3) المصلدة بالترسيب. إن إمكانية تشكيل سبيكة الألمنيوم (Al-2024-T3) عند درجة حرارة متوسطة مع قابلية تشكيل مقبولة ومقاومة شد أعلى لأجزاء الهياكل يعتبر أفضل مقارنة بنفس السبيكة في ظرف التلدين التام. ER -