@Article{, title={IMPACT MODIFIER OF EPOXY RESIN WITH CITRACONICIATED POLYBUTADIENE AS TOUGHENING AGENT}, author={A. A. Sultan(1), A.A.Ateik(1) , and Moayad N. Khalaf(2)}, journal={Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد}, volume={10}, number={2}, pages={304-309}, year={2010}, abstract={The impact strength of epoxy resin based on diglycidyl ether of bis phenol-A- with citraconiciated polybutadiene were investigated. The polybutadiene citraconiciated by reaction with citraconic anhydride and benzoyl peroxide as initiator. The percent citraconiciation was 10%.In the present work citraconiciated polybutadiene was used as impact modifier for epoxy resin. The percentage of the blend between citraconiciated polybutadiene and epoxy resin was (5, 7.5, 12.5, and 20%) while the amine hardener of the epoxy resin was added at a ratio of 1 part amine to 3 part epoxy.

تم في هذا البحث تحضير بولي بيوتاداين بمجاميع من الستراكونيك بنسبة 10% وذلك بمفاعلة البولي بيوتاداين مع الستراكونيك اللامائي بوجود بيروكسيد البنزويل كبادئ للتفاعل. تم أستخدام البولي بيوتاداين المطعم بالستراكونيك كمحسن لقوة الصدم للأيبوكسي بعد أن مزج مع اللأيبوكسي بالنسب ( 5 , 7.5 , 12.5 , 20 % ) بينما كانت نسبة المصلب الأميني الى اللأيبوكسي هي جزء واحد من الأمين وثلاثة أجزاء من الأيبوكسي.أظهرت النتائج تحسنا" واضحا" في قوة الصدم للأيبوكسي بزيادة نسب البولي بيوتاداين المطعم بالستراكونيك بسبب زيادة التوافقية بين الراتنج الأيبوكسي و البولي بيوتاداين المطعم بمجاميع الستراكونيك الفعالة.} }