@Article{, title={The influence of the temperature on the ultimate tensile strength of the composite materials at constant Fiber volume fraction تأثيردرجة الحرارة على مقاومة الشد للمواد المتراكبة بثبوت الكسر الحجمي للألياف}, author={Hussain J. Al-alkawi and Dhafir S. Al-Fattal and Abdul-jabar H. Ali}, journal={Engineering and Technology Journal مجلة الهندسة والتكنولوجيا}, volume={30}, number={11}, pages={1935-1947}, year={2012}, abstract={The aim of this work is to study the influence of the temperature on the ultimatetensile strength (UTS) of composite material which is manufactured from polyester andE-glass (woven roving, chopped strand mat) as a laminate with a constant fiber volumefraction (VF) of 33%. The results showed a little effect of temperature on tensilestrength in the range of room temperature (RT) to 50 oC for laminates reinforced withE-glass (woven roving) [0/90, ±45,0/90], [0/90]3, and [0/90, CSM, 0/90], but forlaminates reinforced with E-glass chopped strand mat (CSM), as [CSM] 3 and [CSM,0/90, CSM], a continuous reduction in strength was observed with increasingtemperature from (RT) to 60 oC. The highest percentage reduction in strength was 23%at 60oC as compared with (RT) for [CSM]3 laminate
بهدف هذا البحث الى دراسة تأثير درجات الحراره على مقاومةالشد للمواد المتراكبه المصنعه من البولستر والالياف الزجاجيه وبنسبه حجميه ثابتة للألياف الزجاجية مقدارها 33 %. أظهرت نتائج 0/90 ] تتأثر قليلا ]3 ,[0/90, CSM, 0/90], [0/90, ±45, 0/ البحث ان المواد المصنعه من ,[ 90 بدرجات الحراره ما في مدى ( درجة حرارة الغرفة و 50 درجه مئويه) في حين ان المواد المصنعه تظهر انخفاض مستمر في اجهاد الشد الاقصى مع زيادة [CSM]3 ,[CSM, 0/90, CSM] من درجة الحراره من درجه حرارة الغرفة الى 60 درجه مئويه وان اعلى نسبة انخفاض لمقاومة الشد كان مقدارها 23 % وذلك عند 60 درجه مئويه مقارنة بمقاومة الشد عند درجه حرارة الغرفة وللماده . [CSM] المصنعه من 3} }