TY - JOUR ID - TI - The influence of the temperature on the ultimate tensile strength of the composite materials at constant Fiber volume fraction تأثيردرجة الحرارة على مقاومة الشد للمواد المتراكبة بثبوت الكسر الحجمي للألياف AU - Hussain J. Al-alkawi AU - Dhafir S. Al-Fattal AU - Abdul-jabar H. Ali PY - 2012 VL - 30 IS - 11 SP - 1935 EP - 1947 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - The aim of this work is to study the influence of the temperature on the ultimatetensile strength (UTS) of composite material which is manufactured from polyester andE-glass (woven roving, chopped strand mat) as a laminate with a constant fiber volumefraction (VF) of 33%. The results showed a little effect of temperature on tensilestrength in the range of room temperature (RT) to 50 oC for laminates reinforced withE-glass (woven roving) [0/90, ±45,0/90], [0/90]3, and [0/90, CSM, 0/90], but forlaminates reinforced with E-glass chopped strand mat (CSM), as [CSM] 3 and [CSM,0/90, CSM], a continuous reduction in strength was observed with increasingtemperature from (RT) to 60 oC. The highest percentage reduction in strength was 23%at 60oC as compared with (RT) for [CSM]3 laminate

بهدف هذا البحث الى دراسة تأثير درجات الحراره على مقاومةالشد للمواد المتراكبه المصنعه من البولستر والالياف الزجاجيه وبنسبه حجميه ثابتة للألياف الزجاجية مقدارها 33 %. أظهرت نتائج 0/90 ] تتأثر قليلا ]3 ,[0/90, CSM, 0/90], [0/90, ±45, 0/ البحث ان المواد المصنعه من ,[ 90 بدرجات الحراره ما في مدى ( درجة حرارة الغرفة و 50 درجه مئويه) في حين ان المواد المصنعه تظهر انخفاض مستمر في اجهاد الشد الاقصى مع زيادة [CSM]3 ,[CSM, 0/90, CSM] من درجة الحراره من درجه حرارة الغرفة الى 60 درجه مئويه وان اعلى نسبة انخفاض لمقاومة الشد كان مقدارها 23 % وذلك عند 60 درجه مئويه مقارنة بمقاومة الشد عند درجه حرارة الغرفة وللماده . [CSM] المصنعه من 3 ER -