TY - JOUR ID - TI - Effect of Heat Treatments on Sliding Wear Behavior of Medium Carbon Steel تاثير المعاملات الحرارية على سلوك البلى الانزلاقي لفولاذ متوسط الكاربون AU - Ahlam Abdalamir Mohamed احلام عبدالامير محمد علي PY - 2012 VL - 30 IS - 13 SP - 318 EP - 328 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - The aim of this work is to study the effect of heat treatments on the wear rate ofthe medium carbon steel which included normalizing and different quenchingmedia (air, oil, salt solution at concentration %25). Quenching Include heating toa temperature of 870Co and then rapid cooling. A Pin -on-Disc technique was usedto measure the wear rate under dry sliding conditions with applied and differentsliding times with constant sliding speed of disc (641 r.p.m) and hardness of thesteel disc (48 HRC).The results show that the wear rate increases with applied loads, and withincreasing sliding time for all heat treated specimens it was found that the hardnessvalues of the quench specimens at salt solution is higher than that of normalizedspecimens and quenched specimens in the oil.

تضمن هذا البحث دراسة تاثير المعاملات الحرارية على معدل البلى الانزلاقي لفولاذمتوسط الكاربون وهي المعادلة والتقسية باوساط تقسية مختلفة (الزيت، محلول ملحيبتركيز 25 %). وتضمنت التقسية التسخين عند درجة حرارة ( 870 ) م° ثم التبريد السريع لكللقياس معدل البلى (Pin – on Disc) العينات المقساة ، وقد استخدمت تقنية المسمار على القرصتحت ظروف الانزلاق الجاف وعند تسليط احمال مختلفة وتثبيت زمن الانزلاق ، وفترات انزلاقHRC ) مختلفة مع تثبيت سرعة الدورانية للقرص( 641 ) دورة/دقيقة وصلادة القرص الفولاذي48 ). وقد اظهرت النتائج ان معدل البلى يزداد بزيادة الحمل المسلط والفترة الزمنية للانزلاقلجميع العينات المعاملة حراريا واظهرت النتائج ان قيم الصلادة للعينات المقساة بالمحلول الملحياعلى من العينات المقساة بالزيت والعينات المعاملة بالمعادلة. ER -