TY - JOUR ID - TI - Effect of Zinc Addition on the Density and Wear Rate of Al-12Si Compacts تأثیر إضافة الزنك على الكثافة والبلى لسبیكة Al-12Si AU - Mahde Mter Hanoon مھدي مطر حنون PY - 2012 VL - 30 IS - 18 SP - 382 EP - 391 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - This research aimed to prepareAl-12Si alloys by powder metallurgy method because of itscommercial and technological importance. Aluminum and Silicon powders were used, thenmixed and blended together and classified into four parts, carbon powder was added to thethree parts (5,10 and 15% wt) and the last remain as it is. These powders were mixed toensure a good distribution of Zinc powder, and then they compacted in is ostatic cold pressureat 10 ton, the compact samples were sintered in furnace under argon gas at 530°C for onehour, These samples were then prepared (grinded, polished and etched) for them icrostructureexamination, density, porosity, microhardness, X-ray diffraction and wear resistance. Theresults showed anincrease in the density and the hardness with addition ratio.

بطریقة میتالورجیا المساحیق (Al-12Si) یھدف ھذا البحث الى تحضیر سبائك المنیوم- سیلیكونتم العمل في ھذا البحث استخدام مسحوقي الألومنیوموالسیلیكون ثم خلطھم وتصنیفھم Powder Metallurgy5,10 ) للأجزاء and 15% wt) تم اضافة مسحوق الزنك بنسب ثلاث .(Al-12Si) الى أربعة أجزاء بنسبةالثلاثةعلى التوالي بینما بقي الجزء الأخر بدون إضافة تم بعدھا اجراء عملیة المزج للأجزاء الثلاثة الأولى10 ) وبقوالب ذات ton) لضمان تجانس مسحوقالزنك مع الخلیط وبعدھا تم إجراء عملیة الكبس على البارد عند530° ) ولمدة ساعة واحدة وباستخدام غاز C) ابعاد مختلفة. تم إجراء عملیة التلبید للعینات المكبوسة عندالأركون كغاز خامل وبعد عملیة التبرید تم تحضیر العینات (الصقل والتنعیم والأظھار) لأجراء فحص البنیةالمجھریة وفحص الكثافة والمسامیة والصلادة وفحص الأشعة السینیة ومقاومة البلیان، وأظھرت النتائج زیادةفي الكثافة والصلادة ومقاومة البلى مع زیادة نسبة إضافة مسحوق الزنك. ER -