TY - JOUR ID - TI - Fabrication of Te Micro-Tubes and TeO2 Micro-Wires From Powders by Cold Spray تصنیع أنابیب التیلیریوم المایكرویة وأسلاك أوكسید التیلیریوم المایكرویة من المساحیق بواسطة الرش على البارد AU - Mohammed S. Hamza AU - Alaa A. Abdul alhameed AU - Sinan salman Hamdi PY - 2012 VL - 30 IS - 19 SP - 3457 EP - 3466 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - A one-dimensional micro-structured tellurium (Te) microtube and telluriumdioxide (TeO2) microwire were successfully prepared by cold spray process inlarge scale by a facile approach of sprayed (Te), (TeO2) dry powder in an inertatmosphere using helium gas onto glass substrate. Tellurium and Tellurium dioxidewere sprayed by heating carrier gas at (200,300,400 and 500 °C) and 2 MPapressure on the glass substrate (100°C). Heat treatment was done under vacuum(0.0133mbar) for (30 min) at (200°C) for Te and (400°C) for TeO2.The preparedmicrotubes and microwire was examined by XRD, AFM and SEM. The resultshowed that the obtained microtubes and microwire were highly pure.

كأنابیب مایكرویة (Te) تم في ھذا البحث تحضیر تراكیب مایكرویة أحادیة البعد من التیلیریومكأسلاك مایكرویة بنج اح بتقنی ة ال رش عل ى الب ارد بم د و ىا س ع ع ن (TeO و أوكسید التیلیریوم ( 2في جو خامل باستعمال غاز الھیلیوم على قواعد من (TeO2 ،Te) طریق الرش الجاف للمساحیقشرائح زجاجیة . تم رش التلیریوم وث اني أوكس ید التلیری وم بتس خین الغ زاِ الحام ل عن د درج ة 500100° ). ت م أج راء C) عل ى قواع د زجاجی ة بدرج ة MPa 200,300,400 ) وض غط 2 , °C)30 ) وب درجات min) 0.0133 ) ولم دة mbar) المعاملة الحراری ة باس تخدام ف رن تل دین ب الفراغالأنابی ب .(TeO 400 ) ل مادة ( 2 oC) بینما استعمل درجة ح رارة (Te) 200 ) لعنصر oC) حرارة.SEM و FM و XRD االمایكرویة المصنعة و الأسلاك المایكرویة المص نعة ت م فحص ھا بواس طةبینت النتائج أن ھذه الأنابیب الرقیقة و الأسلاك الرقیقة كانت ذات نقاوة عالیة. ER -