TY - JOUR ID - TI - MECHANICAL PROPERTIES OF POLYSTYRENE RESIN REINFORCED BY ARAMID FIBERS الخواص الميكانيكية لراتنج البولي ستايرين المقوى بألياف الأرمايد AU - Mahmoud A. Hassan محمود عبد حسان PY - 2013 VL - 6 IS - 1 SP - 1a EP - 5a JO - Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية SN - 19984456 24117773 AB - In this research the effect of the reinforcement by fibers on Mechanical properties of polystyrene resin reinforced by aramid fibers was studied .The properties included impact strength , tensile strength Where the Mechanical properties were extracted for polystyrene resin before reinforcement by fibers, then we reinforced the resin by different weight percentage from aramid fibers (%15,%30, %45, %60)and studied the effect on the above mechanical properties. An Improvement was happened in these properties after reinforcement by fibers The value of mechanical properties will increase with increasing percentage of reinforcement . Impact strength increased from(8Kj/m2) to (160Kj/m2) and compressive strength from (37Mpa) to (328Mpa) for reinforcing percentages 0% and 70% respectively .

تم في هذا البحث دراسة تأثير التقوية بالألياف على الخواص الميكانيكية لراتنج البولي ستايرين المقوى بألياف الأرمايد . لقد شملت هذه الخواص كل من مقاومة الصدمة ومقاومة الشد حيث تم في البداية إستخراج الخواص الميكانيكية لراتنج البولي ستايرين قبل وبعد التقوية بالألياف ، حيث تم تقوية الراتنج بنسب وزنية مختلفة من ألياف الأرمايد (%60,%45, %30, %15) و دراسة تأثير ذلك على الخواص المذكورة. حصل تحسن في قيمة هذه الخواص بعد التقوية بالألياف إضافة إلى زيادة قيمة هذه الخواص مع زيادة نسبة التقوية بالألياف . فبالنسبة لمقاومة الصدمة إرتفعت من (8Kj/m2) إلى (160Kj/m2) ومقاومة الشد من (37Mpa) إلى (328Mpa) ولنسب التقوية 0% و 60% على التوالي . ER -