TY - JOUR ID - TI - Immunohistochemical detection to evaluate the biological role of Ti implants coated by a combination of fibronectin protein and hydroxyapitate (EPD) (in vivo study) AU - Athraa Y.Al-Hijazi عذراء يحيى الحجازي AU - Thair L-Al-Zubaydi ثائر الزبيدي AU - Eman I. Mahdi ايمان مهدي PY - 2012 VL - 24 IS - 2 SP - 32 EP - 38 JO - Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد SN - 18171869 23115270 AB - Background: physicochemical and biochemical coating techniques that are investigated now a day to enhancebone regeneration at the interface of titanium implant materials. The combination, however, of both organic andinorganic constituents is expected to result into truly bone-resembling coatings and as such to a new generation ofsurface-modified titanium implants with improved functionality and biological efficacy. This research was conductedto study the expression of osteocalcin and growth hormone receptor as bone formation markers in coated anduncoated implant in interval periods (3days,1,2and 6 weeks).,Materials and methods: Commercially pure titanium (CpTi) implants coated with hydroxyapatite by EPD method andwith fibronectin protein, were placed in the tibia of (16) New Zeland white rabbits , immunohistochemical tests fordetection of expression of osteocalcin and growth hormone receptor were performed on all the implants of bothcontrol and experimental groups (3days,1,2 and 6 weeks) healing intervals. Mechanical test (torque removal test)was performed as an indicator for the presence of osseointegration and as a test for the mechanical property ofbone-implant interface to be primarily propping the interface machanics.Results: The removal torque mean values in all studied groups uncoated and coated were increasing withadvancing time (higher at 6 than 2 weeks periods) and coated implant showed high value in comparsion to control.Result shows that Immunohistochemical findings revealed high positive expression range from strong to moderate forosteocalcin and growth hormone receptor in coated implant in comparison to uncoated. These results indicatingthat a mixing of bioactive HA ceramic and FN increased the activity of coated layer which improved the boneformation and maturation in bone-implant interface and enhance mechanical interlocking with bone.Conclusions: The present study concludes that organic and inorganic surface modification for titanium implantsurface by HA and FN enhances bone formation and increase osseointegration

ER -