TY - JOUR ID - TI - Effect of Fiber Volume on The Flexural Strenght of Steel Fiber Reinfored Polyester Resin Composite تأثير الكسر الحجمي في متانة الالتواء لمتراكبات البولي استير المدعم بالياف الحديد AU - Harith I.Jaffer حارث ابراهيم جعفر AU - Awattif A Mohammed عواطف عذاب محمد AU - Ban M.Al-Shabander بان مازن الشابندر PY - 2013 VL - 54 IS - 1 SP - 105 EP - 109 JO - Iraqi Journal of Science المجلة العراقية للعلوم SN - 00672904 23121637 AB - The aim of this study is to determine the flexural properties of steel fiber as a metal fiber and polyester resin as a matrix. The steel fibers were added to polyester resin at the various fiber volume fractions of 5, 10, and 15% steel fiber, and with different fiber orientations such as woven steel fiber type (0-45) ° and woven steel fiber type (0-90) ° indicate. Hand layup processes in these experiments were used to produce specimens test with the curing time of 24 hr. for the composite at room temperature. The results show that the flexural strength and flexural modulus values for 15 % vol.of woven steel fiber composite type (0-90) ° are (210MPa) and (2.29GPa( respectively. The results above indicate that the woven steel fiber (0-90) ° has a better bonding between its fiber and matrix compare to woven steel fiber type (0-45) °.

الهدف من هذه الدراسة هو تحديد خواص الالتواء لالياف الحديد كالياف معدنية وراتنج البولي استير كمادة اساس . الياف الحديد اضيفت الى راتنج البولي استير بكسور حجمية مختلفة هي 10,5و15% , مع اختلاف في اتجاه الالياف مثل حصيرة الالياف نوع (0-45) ° وحصيرة الالياف نوع (0-90) ° .تم تصنيع الواح من المتراكبات بطريقه التصنيع اليدوي مع زمن تصلب مقداره 24 ساعه بدرجه حرارة الغرفة.اظهرت النتائج قيم متانه الالتواء ومعامل الالتواء للكسر الحجمي 15% لمتراكبات حصيرة الياف الحديد نوع (0-90) °هي (210MPa)و((2.29GPa على التوالي.وبينت النتائج اعلاه ان حصيرة الالياف من نوع (0-90) ° تمتلك اليافها ترابط افضل مع المادة الاساس مقارنه لحصيرة الالياف نوع ° (0-45) . ER -