TY - JOUR ID - TI - Effect of Zn Substitution on thestructural Properties of Cobalt Ferrite Nano Particles Prepared Via Sol-Gel Route تأثير تعويض الزنك على الخواص التركيبية لفرايت الكوبلت ذو الدقائق النانوية والمحضر بالطريقه (sol-gel ). AU - Tahseen H. mubarak تحسین حسین مبارك AU - Sabah M Ali صباح محمد علي AU - Laith S Mahmood ليث شاكر محمود PY - 2013 VL - 9 IS - 1 SP - 56 EP - 62 JO - Academic Science Journal مجلة العلوم الاكاديمية SN - 83732222 25189255 AB - Zinc substituted cobalt ferrite nanoparticles (CoxZn1-xFe2O4, with x = 0.0, 0.1, 0.2, 0.3, 0.4, and 0.5) were prepared via sol-gel route and the effect of zinc concentration on Lattice constant and particle size and powder‎ densitywere investigated. X-ray diffraction analysis confirms the formation of ferrites in nano phase. The Results showed that the particle size decreasing from (22) to (16) nm with increasing the concentration of ‎zinc to the (x= 0.5). The lattice constant increased from (8.36682) to )8.40943)A0 with increasing the concentration of zinc to (x = 0.5), while the theoretical powder‎ density decreased from (5.3225) to (5.2237) g/cm3 by ‎increasing zinc ion concentration to value at (x=0.5).‎

تم في هذا البحث تحضير فيرايت الكوبالت المعوضة بايونات الزنك ذات السلسلة الفيراتية Co1-xZnxFe2O4), حيث تأخذ xقيم من الصفرالى (0.5 بالطريقة الكيميائية الحديثة(sol-gel auto combustion) المحضرة وأظهرت النتائج بأن حجم دقائق المسحوق يقل حجم من 22 الى 16 نانومتر مع زيادة تركيز ايونات الزنك . إن ثابت الشبيكة يزداد من 8.367 إلى 8.40943 انكستروم بزيادة تركيز ايونات الزنك إلى القيمة (x=0.5 ) .إما بالنسبة لكثافة المسحوق فإنها تقل من (5.3225) غم/سم3 بزيادة تركيز ايونات الزنك وصولا إلى القيمة5.2237 غم/سم3 عند x= 0.5)). ER -