TY - JOUR ID - TI - Effect of nano and micro SiO2 weight percent on interlaminar fracture toughness of woven roving/ epoxy composites دراسة تأثير النسب الوزنية لجزيئات السليكا المايكروية والنانوية على متانة الكسر الطبقية لمتراكبات الايبوكسي المدعمة بالالياف نوع المنتظم AU - Zainab R.Muslem زينب رحيم مسلم AU - Harith I. Jaafer حارث ابراهيم جعفر PY - 2012 VL - 10 IS - 18 SP - 117 EP - 121 JO - Iraqi Journal of Physics المجلة العراقية للفيزياء SN - 20704003 26645548 AB - Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I). Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.

تم في هذا البحث دراسة تاثير اضافة نسب وزنية مختلفة من جزيئات السليكا المايكروية والنانوية على متانة الكسر الطبقية لمتراكبات الايبوكسي المدعمة بالالياف نوع المنتظم المحضرة بتقنية التشكيل اليدوي وبنسب 2 و4 و6 و8 و 10 %. فحصت العينات باستخدام نموذج العتلة المزدوج (النمط الاول) واستخدمت طريقة المساحة لحساب متانة الكسر الطبقية. اظهرت النتائج ان متانة الكسر الطبقية تزداد بزيادة نسبة الجزيئات المضافة وان السبب الرئيسي للفشل في المتراكبا ت المايكروية والنانوية هو التوسعات الطبقية والتي لوحظ انها تقل بزيادة نسب الجزيئات المضافة. ER -