@Article{, title={Evaluation of Using Local Coarse Aggregate of Kerbala Quarries in Production of High Strength Concrete}, author={Najah M. L. Al-Maimuri and Mohammed K. Al Khafaji and Jabbar A. J. Al Khafaji}, journal={Journal of University of Babylon مجلة جامعة بابل}, volume={21}, number={5}, pages={1611-1621}, year={2013}, abstract={The use of White Crushed Gravelfrom Kerbela Quarries in the design of high strength concrete mixes is evaluated through this research. Two grades of mixes are undertaken; they are A (40 Mpa) and B (60 Mpa)of compressive strength. The mixes proportion is used for the design in these mixes are (0.35 and 0.3 water/cement ratio), (446kg/m3 and 550kg/m3 cement), (0.8 liter/kg super plasticizer( for each A and B mixes respectively. The fresh concrete tests results indicate that mixes made of the Crushed White Gravel characterized with slump value of 57 and 52 mm and compaction factor of (0.95, 0.92) for the mixes type A and B respectively.The maximum compressive strength of (43.6and 62.2)Mpa,the modulus of elasticity of (40.5 and 43.4) Gpa, the modulus of rupture of (6.3 and 6.7)Mpa, the splitting tensile strength of (4.5 and 4.9 Mpa, the Ultra Sonic Pulsevelocity of (4.25 and 4.58)Km/sfor both A and B mixes respectively at 28 days.

تم تقييم استخدام الحصى الابيض المكسر من مقالع كربلاء قي تصميم الخلطات الكونكريتية عالية المقاومة. تم تناول نوعين من الخلطات بمقاومة انضغاط(A) (40 Mpa) و B))(60Mpa).ان نسب تصميم الخلطات هو (0.35 و0.3 ماءسمنت), (446كغمم3 , 550 كغمم3), (0.8 لترم3) لكلا الخلطتان A و B على التوالي.ان نتائج فحوصات الخرسانة الطرية بينت ان الخلطتين المصنوعتينمن الحصى الابيض المكسّر كانت باقل هطولومقداره 52 , 57ملم للخلطة ب وعامل رص هو 0.95 ,0.92 للخلطتان A و B على التوالي. ان اعلى مقاومة الانضغاط هي 43.6 و 62.2ميكاباسكال ومعامل مرونة 40.5 و 43.4 كيكا باسكال ومعامل التصدع 6.3 و 6.7 ميكا باسكال ومقاومة شد الانشطار4.5 و 4.9 ميكا باسكال وسرعة الموجات فوق الصوتية هي 4.25و 4.58 كمثانية و لكلا الخلطتين A و B في عمر 28 يوم على التوالي.} }