@Article{, title={Effect of molecular weight on electrical properties of PMMA – TiCl3 composite}, author={Z. Abed Alsalam AL-Ramadhan}, journal={Journal of University of Babylon مجلة جامعة بابل}, volume={21}, number={7}, pages={2555-2564}, year={2013}, abstract={Poly(methyl methacrylate) was prepared with different molecular weight by bulk polymerization (M = 0.578 x 105 , 1.28x105 & 1.64 x 105 g/mole). Film of PMMA with TiCl3 salt additive ranged from (1-5%) cast from chloroform solutions onto glass plates (the films thickness was ~ 100μm) . The experimental results show the relationship between electrical properties & Viscosity average molecular weight. (DC conductivity) increased three order of magnitud with increasing molecular weight, the Eac (activation energy) values accordingly decrease as the average molecular weight increase.On the other hand , increased by several orders of magnitude with increasing TiCl3 content and applied temperature ranged from (40-100)0C. The activation energy is also determined and found to decrease with increasing salt content.

بولي مثيل ميثااكريلايت حضر بطريقة البلمرة وبأوزان جزيئية مختلفة0.578 x 105 , 1.28x105 =M) .(g/mole 1.64 x 105 وتم تحضير اغشية من PMMA و TiCl3 وبنسب مختلفة من المضاف تتراوح(1-5%) بطريقة الصب من المحاليل وبسمك .100μm النتائج التجريبية بينت العلاقة بين الخصائص الكهربائية ومعدل الوزن الجزيئي اللزوجي. حيث وجد ان التوصيلية الكهربائية المستمرة ازدادت ثلاث مراتب بزيادة الوزن الجزيئي، وطاقة التنشيط تقل مع زيادة معدل الوزن الجزيئي. من جهة اخرى التوصيلية الكهربائية المستمرة ازدادت عدة مراتب مع زيادة نسبة TiCl3ومدى درجات الحرارة .(40-100)0C. كذلك طاقة التنشيط وجدت مع زيادة نسب الملح المضاف.} }