TY - JOUR ID - TI - IMPROVEMENT OF FLAME RETARDANCY FOR HYBRID COMPOSITE MATERIAL BY USING ZINC BORATE تحسين إعاقة اللّهب لمادة متراكبة هجينة بإستعمال بورات الزنك AU - Ali I. Al-Mosawi &Dr. Abbas A. Al-Jeebory &Dr. Mustafa A. Rijab & Mushtaq T. Al-Bdiry PY - 2013 VL - 13 IS - 3 SP - 565 EP - 569 JO - Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد SN - 20761819 AB - Zinc borate was added as a surface layer of (4mm) thickness on the surface of araldite resin reinforced by woven roving carbon-kevlar fibers .This system was exposed under different exposure intervals (10,15, and 20mm) to a direct flame which generated from oxyacetylene and gas flame (3000ºC,2000ºC) respectively, and study the range of resistance of flame retardant material layer to the flames and protected the substrate . Surface temperature opposite to the flame method was used to measuring the temperature transferred through this system. The experimental results show that a great increment in thermal resistance and flame retardancy after coating by zinc borate and the best percentage was (20%) from zinc borate, as well as rising flame resistance increased exposure intervals to flame

تم إضافة بورات الزنك بشكل طبقة سطحية بسمك (4mm) على سطح راتنج الإرلدايت المقوى بألياف كاربون -كيفلار المحاكة. تم تعريض هذا النظام وبمسافات تعرض مختلفة (20mm,15,10) إلى لّهب مباشر متولد من شُعلة أُوكسي أستلينية وشُعلة غازية بدرجة حرارة 3000ºC) (2000ºC, على التوالي ، ودراسة مدى مقاومة طبقة المادة المعيقة للّهب لحرارة الشُعلتين ومدى حمايتها للمادة المتراكبة الواقعة تحتها . تم إعتماد طريقة قياس درجة حرارة السطح المقابل للشعلة في قياس درجة الحرارة المنتقلة خلال هذا النظام . أظهرت نتائج الإختبارات العملية زيادة كبيرة في المقاومة الحرارية وإعاقة اللّهب للمادة المتراكبة بعد طلائها ببورات الزنك وأفضل زيادة كانت عند نسبة (%20) من بورات الزنك ، إضافة إلى إرتفاع مقاومة اللّهب مع زيادة مسافة التعرض للشُعلة الحرارية . ER -