TY - JOUR ID - TI - Experimental Investigation and Mathematical Modeling of Tensile Properties of Unsaturated Polyester Reinforced by Woven Glass Fibers التقصي العملي والنمذجه الرياضيه لخصائص الشد للبولي استر الغير مشبع المقوى بالياف الزجاج الحصيرية AU - Jawad Kadhim Oleiwi AU - Emad Saadi Al- Hassani AU - Alaa Abd Mohammed PY - 2014 VL - 32 IS - 3 Part (A) Engineering SP - 653 EP - 666 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - This research studied the tensile properties of glass fiber reinforced unsaturated polyester with different fiber volume fraction Vf, and angle of fibers for coarse and fine woven fibers reinforcement. The composite specimens were prepared by hand lay-up technique and cutting according to (ASTM D – 638) for tensile test to obtain modulus of elasticity, ultimate tensile strength and elongation percentage of the composite specimens. Mathematical models were done by using statistical analysis which shows the tensile properties of the composite specimens as a function of volume fraction and fiber angle.The results show that the maximum value of the modulus of elasticity was (11.5 GPA) and the maximum value of ultimate tensile strength was (240 MPa) which happed at (11% VF) for fine woven fibers and for (0º/90º) fibers angle, and vice versa for percentage elongation was (2.5%).

في هذا البحث تم دراسة خواص الشد للبولي استر غير مشبع مقوى بالياف الزجاج عند تغير كل من الكسر الحجمي وزاوية الليف لنوعين من التقوية الحصيرة الخشنه والناعمه. حضرت العينات المركبة بالطريقة اليدوية وقطعت وفق المواصفه (ASTM D – 638) لفحص الشد للحصول على معامل المرونة واقصى أجهاد شد والاستطالة النسبية لهذه العينات. تم عمل نماذج رياضية باستخدام التحليل الأحصائي الذي يبين خواص الشد كدالة لكسر الحجمي وزاوية الليف. بينت النتائج بان اقصى قيمة لمعامل المرونة كانت(11.5 GPa) واقصى اجهاد شد كان(240 MPa) يحصلان عند الكسر حجمي (11%) عند التقوية بالحصيرة الناعمة ولزاوية ليف (0º/90º) والعكس بالعكس للاستطاله النسبية حيث كانت 2.5%) ). ER -