TY - JOUR ID - TI - الاكسدة الضوئية المحفزة لمبيد Paraquat dichloride بأستخدام العامل المساعد الجديد كرومات اوكسيد النيكل ( NiO-Cr2O3) في الانظمة المائية AU - ندى يحيى فيروز AU - علاء رشيد عمران PY - 2014 VL - 22 IS - 8 SP - 2161 EP - 2169 JO - Journal of University of Babylon مجلة جامعة بابل SN - 19920652 23128135 AB - Paraquat dichloride, a herbicide that is always polluting our water system. Thus a lot of efforts has been conducted to treat the polluted water. In this study , Nickel oxide chromateis used as photocatalyst to degrade the paraquat dichloride in the presence of UV light ((λ=354 nm) . the photodegradation rate was measured by used UV-1650PC Shimadzu spectrophotometer. Paraquat dichloride showed the maximum absorption band at(λ=633nm) . As shown in results the best ratio of coupled from chromium oxide and nickel oxide in photocatalyst to degradation paraquat solution was NiO:CrO3 %weight ratio 1:0.18. and the optimum photocatalyst calcinations temperature for degradation paraquat dichloride was 700C0 . The best %weight of catalyst required to degred 3.7×10-3M of solution paraquat dichloride was (1g/L) while the best PH was under reang (7-9).

Paraquat dichloride مبيد حشائش غالبا ما يلوث نظامنا المائي , لذا يجب تظافر الجهود لمعالجة هذا التلوث, وفي هذا البحث تم تحضير كرومات اوكسيد النيكل كعامل مساعد جديد استخدم في تكسير هذا المبيد بوجود الضوء فوق البنفسجي (λ =354 nm) . تم متابعة سرعة التكسير الضوئي باستخدام جهاز UV-1650PC Shimadzu spectrophotometer, حيث اظهرالمبيد اعظم امتصاص عند الطول الموجي(λ =633nm) , لقد اظهرت النتائج بان افضل نسبة مزج من اوكسيدي النيكل والكروم لتكسير المبيد هي بنسبة وزنية (1:0.18) NiO:CrO3 , وفضل درجة حرارة تحميص كانت 700C0, اضافة الى ذلك وجد بان افضل وزن لازم لتكسير المبيد بتركيز 3.7×10-3M هو (1g/L) وافضل دالة حامضية (PH=7-9). ER -