تأثير التعويض الجزئي ل Ag و Sr على الخواص التركيبية للمركب Tl2-xAgxBa2¬-ySryCa2Cu3O10+ الفائق التوصيل الكهربائي عند درجات الحرارة العالية

Abstract

Subhi.S.R1,Khaled.H.M2, Abdul Salam .S.B2Unversity of Tikreet, College of Engeerning,Dept of Electreic1Unversity of Tikreet, College of Education,Dept of Physics2Abstract: The sample of high temperature superconductivity of type Tl-2223 ( Tl2 Ba2Ca2Cu3O10+ ) have been prepared by using solid state reaction method . The samples have been prepared at the sintering temperature (840o C) for (24h ) at average heating rate( 2o C/ Min ) and hydrostatic pressure (8 ton / cm2).The partial substitution effect of(Ag) in (Tl) and ( Sr ) in ( Ba ) in the compound as(Tl2Ba2¬-ySryCa2Cu3O10+ ) has been investigated where (x= y= 0.1, 0.2 and 0.3). The X-Ray diffraction patterns were obtained , the compound has been characterized as ( Tl-2223 ) having tetragonal structure with lattice parameters ( a=b=3.91 ) and (c= 33.54 for ( x=y=0 ). Also the X-Ray diffraction data showed that the structure of the compound is tetragonal phase in the rang

Keywords

حضرت عينات فائقة التوصيل عند درجات الحرارة العالية من النوع, 2223Tl, Tl2-xAxBa2¬-ySryCa2Cu3O10+, بطريقة تفاعل الحالة الصلبة, وعند درجة الحرارة التلبيد, 840o C لمدة, 24h بمعدل تسخين, 2o C/min وضغط هيدروستاتيكي, 8 ton /, أظهرت دراسة حيود الاشعة السينية, XRD للمركب, Tl2223 انه ذو تركيب بلوري من نوع الرباعي القائم, Tetragonal وذات ابعاد شبيكة, a=b=3.91 و, c=33.54 . وكذلك تم دراسة تأثير التعويض الجزئي للعنصر, Sr في, Ba وبنسب مختلفة ل, 0.1, 0.2, 0.3 حيث, x=y وقد أظهرت نتائج الدراسة من خلال فحص التركيب البلوري للمركب بان التركيب يبقى محافظا على النوع الرباعي القائم ضمن المدى, ..